  • Biocompatibility of Chitosan-g-Poly(2-Hydroxyethyl Metacrylate) Membranes
  • Kim KS, Cho SH, Chun YC, Shin JS, Kim KH, Lim JS
  • Chitosan-g-Poly(2-Hydroxyethyl Methacrylate) 그라프트 공중합체막의 생체적합성
  • 김공수, 조석형, 전용철, 신재섭, 김경호, 임정수
Abstract
The membranes of acetylated chitosan-g-poly (2-hydroxyethyl methacrylate) were prepared for a skin substitute, and water content, tensile strength, elongation, permeability of water vapor and oxygen, and biodegradability of the membrane was determined. The water absorption was 130∼460%, and the tensile strength(242∼506 kg/cm2) was higher than that of the normal skin. The coefficients of water vapor and oxygen permeability were 7.4×10-9∼3.4×10-8(g·cm·cm-2s-1) and 1.4×10-8∼3.17×10-7(cm3(STP)cm·cm-2s-1cmHg-1), respectively. The biodegradation rate was fast at the initial state, but it became slower after 9∼10 days.

chitosan-poly(2-hydroxyethyl methacrylate) 그라프트 공중합체를 막으로 제조하고 그 막을 아세틸화 한 후 인공피부로서의 사용가능성을 검토하기 위하여 흡수성, 기계적 성질, 수증기 및 산소 투과성, 효소에 의한 생분해성등을 검토하였다. 흡수성은 130∼460%였고 기계적 강도는 242∼506 kg/㎠으로서 정상피부 보다 높은 값을 보였으며, 수증기 및 산소 투과성은 7.4×10-9∼3.4×10-8(g·cm·cm-2s-l)과 1.4×10-8∼3.17×l0-7 (cm3(STP) cm·cm-2s-l·cmHg-l)이었다. 효소에 의한 생분해성은 9∼10일 까지는 빠르게 증가하였으나 그 이 후는 거의 증가하지 않았다.

References
  • 1. Hall CW, Spira M, Gerow F, Adams L, Martin E, Hardy SB, Trans. Am. Soc. Artif. Intern. Organs., 16 (1977)
  •  
  • 2. Capozza RCEnzymically Decomposable Biodegradable Pharmaceutical Carrier, Ger. Pat., 2, 505, 305 (1975)
  •  
  • 3. Wistler RJ, Kosik M, Arch. Biochem. Biopolym., 142, 106 (1971)
  •  
  • 4. Kojima K, Iguchi S, Kajima Y, Yoshikumi M, J. Appl. Polym. Sci., 28, 87 (1983)
  •  
  • 5. Bloch R, Burger MM, Biochem. Biophys. Res. Commun., 58, 13 (1974)
  •  
  • 6. Bough WA, Food Product Develop., 11, 90 (1977)
  •  
  • 7. Muzzarelli RAAChitin, Pergamon Press Ltd., p. 257 (1977)
  •  
  • 8. Creighton CP, Teschemacher CRU.S. Patent, 4,109,074 (1978)
  •  
  • 9. Nathan P, Law EJ, Macmillan BG, Murphy DF, Ronel SH, Andrade JD, Abrhans RA, Trans. Am. Soc. Artif. Int. Organs., XXII, 30 (1986)
  •  
  • 10. Tollar M, Stol M, Kliment K, J. Biomed. Mater. Res., 3, 305 (1969)
  •  
  • 11. Lee PI, J. Control. Release, 4, 1 (1986)
  •  
  • 12. Cho SH, Kim KS, Kim KH, Shin JS, Polym.(Korea), 14(1), 9 (1990)
  •  
  • 13. Aiba SI, Minoura N, Fujiwara Y, Kobunshi Ronbunshu, 36, 299 (1982)
  •  
  • 14. Aiba S, Minoura N, Fujiwara Y, Kobunshi Ronbunshu, 39, 299 (1982)
  •  
  • 15. Kim JH, Kim KY, Polym.(Korea), 8(2), 98 (1984)
  •  
  • 16. Homsy CA, J. Biomed. Mater. Res., 4, 341 (1970)
  •  
  • 17. Tokura S, Nishi N, Nishimura S, Sonorin O, Sen-I Gakkaishi, 39, 45 (1983)
  •  
  • 18. Balassa LL, Prudden JFProc. 1st International Conference Chitin/Chitosan, MIT, p. 296 (1977)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1990; 14(4): 385-391

    Published online Aug 25, 1990