Three block copolymers are studied in PS / PE blends in terms of mechanical properties. Block copolymers tested are two diblock S-E and S-EP, and a triblock S-EB-S. Tensile strength and elongation are mechanical properties measured with block copolymer level in both PS/HDPE and PS/LDPE blends. Of three block copolymers examined, diblock S-E and triblock S-EB-S improve tensile strength of PS/HDPE and PS/LDPE blends significantly, exhibiting a maximum tensile strength at 2 wt. % level. Elongation at break is also enhanced by S-E and S-EB-S but it is increased with block copolymer level. Improvement in tensile strength and elongation by S-E and S-EB-S is much more noticeable in PS/HDPE blends than in PS/LDPE. In general, S-E outperforms S-EB-S. The diblock S-EP, however, gives little effect on the tensile strength and elongation of PS/PE blends. It is speculated that non-crystalline EP block is responsible for this Since the non-crystalline EP block is not compatible with crystalline PE phase, there may be a new interface formed between EP block and PE phase.

PS/PE 블렌드에서 세 블록 공중합체의 영향을 기계적 성질로써 연구하였다. 시험한 블록 공중합체는 두 가지 diblock S-E와 S-EP이고, 하나의 triblock S-EB-S이다. 인장강도와 연신률이 측정한 기계적 성질인데, PS/HDPE, PS/LDPE 블렌드에서 블록 공중합체의 함량에 따라 측정하였다. 시험한 세 공중합체 중에서 diblock S-E와 triblock S-EB-S는 PS/HDPE 및 PS/LDPE 블렌드의 인장강도를 크게 향상시켰다. 그러나 두 블록 공중합체 공히 2%에서 최고의 인장강도를 주고 있다. 파단시 연신률도 두 블록 공중합체에 의해 향상되고 있는데, 공중합체의 함량에 따라 계속 증가하였다. S-E와 S-EB-S 공중합체에 의한 인장강도와 연신률의 향상은 PS/LDPE 블렌드보다 PS/HDPE에서 더 크게 나타났다. 전반적으로 S-E가 S-EB-S보다 더 좋은 향상을 보였다. 그러나 diblock S-EP는 PS/PE 블렌드의 인장강도와 연신률을 증가시키지 못했다. 이 이유는 비 결정성 EP 블록이 결정성 PE상과 상용성이 없어, 두 상간에 새로운 계면이 형성되기 때문이라 생각된다.