The CaCO₃ was treated with microencapsulation, coupling agent (KR-TTS) and acrylic acid monomer to improve the adhesion of interface and dispersion of fillers in the particulated filler/polymer composite system. The physical properties of HDPE filled with surface treated CaCO₃ were measured by the mechanical, rheological and dynamic mechanical methods. And the effects of surface treatment were evaluated. In microencapsulation, it was known that formation ability and shape of microcapsules had more or less difference according to the used polymeric wall materials. ratios of formation and shape of fillers. In effects of surface treatment. mechanical and dynamic mechanical properties were improved in order of acrylic acid monomer treatment, microencapsulation and coupling agent (KR-TTS) treatment. On the other hand, rheological properties were improved in order of coupling agent treatment, microencapsulation and acrylic acid monomer treatment.

분산계 복합재료에 있어서 계면의 친화성과 충전제의 분산성을 향상시키기 위해 탄산칼륨을 마이크로 캡슐화, 커플링제 처리(KR-TTS) 그리고 중합성 단량체(AA)에 의한 표면처리로 각각 처리하였다. 표면처리된 탄산칼슘을 충전시킨 HDPE의 물리적 성질을 역학적, 유성학적, 동역학적 측정법으로 측정하여 각 표면처리의 효과를 조사하였다. 새롭게 도입한 마이크로 캡슐화법에 있어서 벽막고분자의 종류와 벽막고분자와 탄산칼슘의 사용비 그리고 충전제의 형태를 달리했을 때, 마이크로 캡슐의 형성능과 형태가 다소 차이를 보였다. 각 표면처리의 효과에 있어서, 계면의 친화성에 의존하는 역학적 성질과 동역학적 성질은 중합성 단량체(AA)에 의한 표면처리, 마이크로 캡슐화, 커플링제 처리(KR-TTS)의 순서로 그 효과를 나타내었다. 그리고 분산성에 의존하는 유성학적 성질은 커플링제 처리(KR-TTS), 마이크로 캡슐화, 중합성 단량체(AA)에 의한 표면처리의 순서로 그 효과를 보였다.