Blends of PVDF and PMMA were prepared by solution-casting method from a 15 weight percent DMF solution. The transitional behavior of PVDF/PMMA blends was examined by differential scanning calorimetry(DSC) over a temperature range from -l00℃ to 200℃ at a heating rate of 10℃/min and by dynamic mechanical measurements from -l20℃ to 150℃ at 1℃/min. PVDF/PMMA blends were judged to be miscible on the basis of the presence of single, composition dependent glass transitions and of the strong melting point depression of the PVDF component. The depression of the PVDF melting point in PVDF/PMMA system judged to be miscible was analyzed using standard thermodynamic arguments to show the exothermic heat of mixing. This exothermic heat of mixing indicated the presence of strong interaction between the binary pairs. All transitions and relaxations were affected by blend composition but in a complex manner owing to the crystallization of PVDF from blends rich in this component. Morphology of fracture surfaces of blends was studied by scanning electron microscopy(SEM) and no signs of phase separation was observed.

용액 casting 방법으로 PVDF와 PMMA의 blend를 15% DMF 용액으로부터 만들었다. PVDF와 PMMA blend의 전이성질을 DSC를 이용하여 l0℃/min의 승온속도로 -100℃에시 200℃의 온도구간에서 조사하였고, 동적 기계적성질을 1℃/min의 승온속도로 -120℃에서 150℃의 온도구간에서 조사하였다. 조성에 관계되는 유리전이온도가 단 하나 존재한다는 사실과 PVDF 성분의 녹는점 강하가 크게 일어난다는 사실로 PVDF와 PMMA가 상용성임을 알았다. 또한 표준 열역학적인 관점에서 PVDF의 녹는점 강하가 혼합열의 발열을 나타냄을 알았고 PVDF와 PMMA가 강력히 결합하였음을 알 수 있었다. PVDF가 많이 함유된 경우, PVDF의 결정화 때문에 모든 전이와 이완은 매우 복잡한 메카니즘에 의해 이루어지며 조성에 크게 의존함을 알았다. 각 blend의 절단 단면의 형태를 SEM으로 조사한 결과 상분리는 일어나지 않았음을 알았다.