Stabilized fibers have been formed from Dralon-T and Acelan by oxidation in air at 200-280℃. From the fibers stabilized for two hours at 260℃, carbon fibers have been obtained by heat treatment in nitrogen at 800-1,200℃. The densities of the PAN precursors have changed from 1.17-1.18g/cm³ to 1.43g/cm³ after two-hour stabilization at 260℃. The stabilized precursor of Dralon-T showed the ultimate density of 1.83g/cm³ after carbonization while that of Acelan showed the 1.76g/cm³. Carbon contents of precursors of both Dralon-T and .Acelan stabilized for two hours at 260℃ were 62.2% and 57.4% in weight, respectively and after carbonization 95.3% and 93.9% in weight, respectively. During stabilization the precursors showed three steps ; shrinkage, expansion and shrinkage in length. However, the load applied on the precursors controlled the degree of the length change.

Dralon-T와 Acelan PAN 섬유를 200∼280℃의 온도로 공기중에서 산화시켜 안정화 섬유를 제조하였다. 이들 중 260℃에서 2시간동안 처리한 안정화 섬유를 질소 분위기에서 800∼1,200℃의 온도로 탄소화 처리하여 탄소섬유를 제조하였다. 밀도 변화를 보면 두 섬유 모두, PAN precursor의 경우에 1.17∼1.18g/cm³였으나 260℃에서 2시간 안정화시킨 후에는 1.43g/cm³로 증가하였고 탄소화 처리 후에는 최대 밀도가 Dralon-T의 경우 1.83g/cm³, Acelan의 경우에는 1.76g/cm³로서 Dralon-T에 의한 탄소섬유의 밀도가 다소 높게 나타났다. 섬유 내의 탄소 함량은 260℃에서 2시간 처 리한 안정화 섬유의 경우에 Dralon-T와 Acelan이 각각 62.2%, 57.4%였으나 1,200℃로 탄소화 처린한 후에는 각각 95.3%, 93.9%로서 Dralon-T의 경우에 탄소 함량이 약간 더 많았다. 안정화 과정 중 섬유의 길이 변화는 초기에 수축을 한다가 신장하고 다시 수축하는 3단계 과정을 거치는데 안정화 처리 온도와 섬유에 부하되는 무게의 영항이 크게 작용을 하는 것으로 나타났다.