  • Analysis of Dynamic and Creep Behaviors of PLA Blends with Blending Ratio
  • Cha JH, Ahn SJ, Jeon HY
  • PLA 블렌드의 조성비에 따른 동역학적 및 크리프 거동 해석
  • 차주희, 안승재, 전한용
Abstract
In the case of poly(lactic acid)/poly(butylene adipate-co-terephthalate) (PLA/PBAT) blend, thermal stability increased as higher PBAT content was blended and it is confirmed that stiffness of PLA/PBAT blend has been improved by increasing the value of storage modulus as addition of CaCO3. From the creep test of PLA/PBAT/CaCO3 blends, the deformation resistance decreased rapidly at lower temperatures as CaCO3 increased. Thus, in the case of application at more than 60 oC, it was considered that PLA/PBAT blend has a high resistance to deformation than pure PLA.

Poly(lactic acid)/poly(butylene adipate-co-terephthalate)(PLA/PBAT) 블렌드의 경우 PLA에 블렌딩된 PBAT의 함량이 커질수록 열안정성이 증가하였으며 CaCO3 첨가에 의한 storage modulus 값의 증가로 PLA/PBAT 블렌드의 강성이 향상되었음을 확인하였다. PLA/PBAT/CaCO3 블렌드의 크리프 변형 결과로부터 CaCO3가 증가할수록 더 낮은 온도에서 시편의 변형 저항성이 급격하게 감소하는 것을 확인하였다. 이로부터 60 oC 이상인 경우 PLA의 단독 사용보다 PLA/PBAT 블렌드를 사용하는 것이 변형에 대한 저항성이 클 것으로 생각된다.

Keywords: PLA/PBAT blend; thermal stability; storage modulus; creep deformation

References
  • 1. Wang LY, Jing XB, Cheng HB, Hu XL, Yang LX, Huang YB, Ind. Eng. Chem. Res., 51(30), 10088 (2012)
  •  
  • 2. Park NH, Kim DH, Park B, Jeong E, Lee JW, Biomater. Res., 17, 114 (2013)
  •  
  • 3. Jiang L, Liu B, Zhang JW, Ind. Eng. Chem. Res., 48(16), 7594 (2009)
  •  
  • 4. Jegal J, Korean Ind. Chem. News, 15(4), 21 (2012)
  •  
  • 5. Yu F, Liu T, Zhao X, Yu Z, Lu A, Wang J, J. Appl. Polym. Sci., 125, E99 (2012)
  •  
  • 6. Li HB, Huneault MA, Polymer, 48(23), 6855 (2007)
  •  
  • 7. Teamsinsungvon A, Rusakulpiwat Y, Jurukumjorn K, Polym. -Plast. Technol. Eng., 52, 1362 (2013)
  •  
  • 8. Teamsinsungvon A, Rusakulpiwat Y, Jurukumjorn K, 18th International Conference on Composite Materials, Edinburgh Scotland (2009).
  •  
  • 9. Jiang L, Wolcott MP, Zhang JW, Biomacromolecules, 7(1), 199 (2006)
  •  
  • 10. Joseph S, Deenadayalan E, Mahanwar PA, J. Polym. Environ.10.1007/s10924-014-0668-5 (2014)
  •  
  • 11. Ljungberg N, Wesslen B, J. Appl. Polym. Sci., 86(5), 1227 (2002)
  •  
  • 12. Georgiopoulos P, Kontou E, Niaounakis M, Polym. Compos., 35, 1140 (2014)
  •  
  • 13. Yu L, Liu HS, Dean K, Chen L, J. Polym. Sci. B: Polym. Phys., 46(23), 2630 (2008)
  •  
  • 14. Widiastuti I, Sbarski I, Masood SH, J. Appl. Polym. Sci., 127(4), 2654 (2013)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2015; 39(4): 566-571

    Published online Jul 25, 2015

  • 10.7317/pk.2015.39.4.566
  • Received on Nov 17, 2014
  • Accepted on Feb 24, 2015