  • Preparation of Syndiotactic Poly(vinyl alcohol) Microfibrils with Radiopaque Inorganic Particles
  • Jo HW, Cha JW, Han SS, Lee JS, Oh TH
  • 방사선불투과성 무기입자를 첨가한 교대배열 폴리비닐알코올 마이크로피브릴의 제조
  • 조혜원, 차진욱, 한성수, 이준석, 오태환
Abstract
Poly(vinyl pivalate) (PVPi) was bulk polymerized to make poly(vinyl alcohol) (PVA) microfibrils to apply for polymeric embolization coils replacing metalic coils. Then, syndiotactic PVA (s-PVA) microfibrils having number-average degree of polymerization of 1100 and s-diad content of 60.4% were prepared via saponification of the PVPi with no separate spinning process. To make s-PVA microfibrils with radiopacity, zirconium dioxide (ZrO2) and barium sulfate (BaSO4) were added into s-PVA microfibrils during saponification. The computed tomography (CT) value indicating radiopacity reached up to over 1000 when the amount of ZrO2 and BaSO4 were 12 and 6 wt%, respectively.

폴리비닐알코올(poly(vinyl alcohol), PVA) 마이크로피브릴(microfibrils)을 금속 색전코일을 대체할 수 있는 고분자 색전코일에 적용하기 위해 벌크중합으로 폴리피발산비닐(poly(vinyl pivalate), PVPi)을 제조하고 비누화 공정에서 방사공정 없이 중합도가 1100 교대배열 다이애드(diad)기 함량 60.4%인 교대배열 PVA(syndiotactic PVA, s-PVA) 마이크로피브릴을 제조하였다. 또한 별도의 조영제의 투여가 불필요한 마이크로피브릴 제조를 위해 방사선불투과성 물질인 이산화지르코늄과 황산바륨을 비누화 공정에서 첨가하여 방사성불투과성 교대배열 PVA 마이크로피브릴을 제조하였고, 무기입자 함유 s-PVA 마이크로피브릴의 computed tomography(CT) value 값 측정 결과 이산화지르코늄의 함량이 12 wt% 이상에서, 황산바륨은 6 wt% 이상에서 1000 이상의 우수한 방사선불투과성을 나타내는 것을 확인하였다.

Keywords: s-PVA; microfibrils; radiopacity; bulk polymerization; embolic materials.

References
  • 1. Lyoo WS, Kim BC, Ha WS, Polym. Eng. Sci., 37(7), 1259 (1997)
  •  
  • 2. Lyoo WS, Ha WS, Polymer, 37(14), 3121 (1996)
  •  
  • 3. Yamaura K, Mizutani I, Monma K, Tanigami T, Matsuzawa SJ, Appl. Polym. Sci., 31, 521 (1986)
  •  
  • 4. Yamamoto T, Seki S, Fukae R, Sangen O, Kamachi MJ, Polym. J., 22, 567 (1990)
  •  
  • 5. Yamamoto T, Yoda S, Takase H, Saso T, Sangen O, Fukae R, Kamachi M, Sato T, Fukunishi Y, Polym. J., 23, 185 (1992)
  •  
  • 6. Yamamoto T, Fukae R, Saso T, Sangen O, Fukae R, Kamachi M, Sato T, Fukunishi Y, Polym. J., 24, 115 (1992)
  •  
  • 7. Kerber CW, Bank WO, Horton JM, Am. J. Roentgenol., 130, 1193 (1978)
  •  
  • 8. Isabelle M, Richard L, J. Neurosurg., 76, 607 (1992)
  •  
  • 9. Kinoshita A, Yamada K, Ito M, Yamazaki M, Teneda M, Hayakawa T, Neuroradiology., 36, 65 (1994)
  •  
  • 10. Brown KT, Brody LA, Decorato DR, Getrajdman GI, J. Vasc. Intev. Radiol., 12, 882 (2001)
  •  
  • 11. Brandrup J, Immergut EH, Editors, Polymer Handbook, 3rd Edn., Wiley, New York (1989)
  •  
  • 12. Lyoo WS, Ha WS, J. Polym. Sci. A: Polym. Chem., 35(1), 55 (1997)
  •  
  • 13. Lyoo WS, Han SS, Kim JH, Yoon WS, Lee CJ, Kwon IC, Lee J, Ji BC, Han MH, Angew. Makromol. Chem., 271, 46 (1999)
  •  
  • 14. Naito R, Kobunshi Kagaku., 15, 597 (1958)
  •  
  • 15. Patel P, Rodriguez F, Moloney G, J. Appl. Polym. Sci., 23, 2335 (1979)
  •  
  • 16. Grubb DT, Kearney FR, J. Appl. Polym. Sci., 39, 695 (1990)
  •  
  • 17. Gurp MV, Int. J. Polym. Mater. Polym. Biomat., 22, 219 (1993)
  •  
  • 18. Lyoo WS, Kim JH, Choi JH, Kim BC, Blackwell J, Macromolecules, 34(12), 3982 (2001)
  •  
  • 19. Choi JH, Ko SW, Kim BC, Blackwell J, Lyoo WS, Macromolecules, 34(9), 2964 (2001)
  •  
  • 20. Vladimir B, Irera B, Lilian HJ, Am. Ceram. Soc. Bull., 80, 982 (1997)
  •  
  • 21. Hammer O, Maurer HJ, Polym. Composite., 19, 116 (1998)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2013; 37(5): 563-570

    Published online Sep 25, 2013

  • Received on Feb 20, 2013
  • Accepted on May 10, 2013