  • Blend Films of Poly(acrylic acid-co-maleic acid) with Poly(vinyl alcohol) (I) : Thermo-mechanical Properties and Gas Permeability
  • Ham SK, Jung MH, Chang JH
  • 폴리(비닐 알코올)과 폴리(아크릴산-말레산) 공중합체의 블렌드 필름 (I)： 열적-기계적 성질 및 가스 투과도
  • 함신균, 정민혜, 장진해
Abstract
Blends of poly(acrylic acid-co-maleic acid)(PAM) with poly(vinyl alcohol)(PVA) were obtained by solution blending. The blends were solvent-on to a film to examine thermo-mechanical properties and gas permeability. The transition temperatures (Tg and Tm) of the blends remained constant regardless of PAM contents. However, the values of enthalpy changes corresponding to melting transition (ΔHm) and initial degradation temperature (TDi) were decreased with increasing PAM content. The values of ultimate strength and initial modulus gave the maximum value at the 12 wt% PAM then decreased with further increase of PAM content up to 15 wt%. To measure the gas permeability of the PVA/PAM blend films, the PVA blend solutions were coated onto both biaxially oriented propylene(BOPP) and poly (ethylene terephthalate)(PET) films. The oxygen transmission rate (O2 TR) permeability values monotonically decreased with increasing PAM content. However, moisture vapor transmission rate was not affected by PAM content.

폴리(비닐 알코올)(PVA)과 폴리(아크릴산-말레산) 공중합체(PAM) 혼합물은 증류수를 사용하여 용액 블렌딩으로 제조하였다. 제조된 블렌드 필름은 다양한 PAM 농도에 따라 변하는 열적-기계적 성질, 모폴로지 및 가스 투과도를 측정하였다. 블렌드 필름의 전이온도(Tg와 Tm)는 PAM의 농도에 관계없이 일정한 값을 가졌다. 그러나, 용융 엔탈피(ΔHm)와 초기 분해온도(TDi)는 PAM 함량이 증가됨에 따라 서서히 감소하였다. 인장 강도와 초기 인장 탄성률은 PAM 함량이 12 wt%일 때 최대값을 나타냈으며, PAM 함량이 15 wt%가 되면 오히려 감소하였다. PVA/PAM 필름의 가스 투과도는 PVA 블렌드 용액을 폴리(에틸렌 테레프탈레이트)(PET)와 이축 연신한 폴리프로필렌(BOPP) 필름 위에 코팅하여 측정하였다. 산소 투과도(O2 TR)는 PAM의 함량이 0~12 wt%까지 증가됨에 따라 코팅된 PET와 BOPP 필름 모두 일정하게 감소하였지만, 수증기 투과도(MVTR)는 첨가된 PAM 농도에 무관하게 일정하였다.

Keywords: poly(vinyl alcohol); poly(acrylic acid-co-maleic acid); blend; film

References
  • 1. Huang RYM, Rhim JW, Polym. Int., 30, 129 (1993)
  •  
  • 2. Levine M, Iikka G, Weis P, J. Polym. Sci. B: Polym. Chem., 2, 915 (1964)
  •  
  • 3. Chiang W, Min C, J. Appl. Polym. Sci., 30, 4045 (1985)
  •  
  • 4. Wen J, Vasudevan VJ, Wilkes GL, J. Sol-Gel Sci. Technol., 5, 115 (1995)
  •  
  • 5. Nakane K, Yamashita T, Iwakura K, Suzuki F, J. Appl. Polym. Sci., 74(1), 133 (1999)
  •  
  • 6. Chuang WY, Young TH, Chiu WY, Lin CY, Polymer, 41(15), 5633 (2000)
  •  
  • 7. Sakurada IPoly(vinyl alcohol) fibers, New York, Marcel Dekker (1985)
  •  
  • 8. Wang CJ, Pang Y, Prasad PN, Polymer, 32, 605 (1991)
  •  
  • 9. Kojima Y, Usuki A, Kawasumi M, Okada A, Kourauchi T, Kamigaito O, J. Polym. Sci. A: Polym. Chem., 31, 983 (1993)
  •  
  • 10. Bassner SL, Klingenberg EH, Am. Ceram. Soc. Bull., 77, 71 (1998)
  •  
  • 11. Olkhov AA, Vlasov SV, Iordanskii AL, Zaikov GE, Lobo VMM, J. Appl. Polym. Sci., 90(6), 1471 (2003)
  •  
  • 12. Chang JH, Jang TG, Ihn KJ, Lee WK, Sur GS, J. Appl. Polym. Sci., 90(12), 3208 (2003)
  •  
  • 13. Yeun JH, Bang GS, Park BJ, Ham SK, Chang JH, J. Appl. Polym. Sci., 101, 591 (2006)
  •  
  • 14. Rhim JW, Hwang HS, Kim DS, Park HB, Lee CH, Lee YM, Moon GY, Nam SY, Macromol. Res., 13(2), 135 (2005)
  •  
  • 15. Nam SY, Sung KS, Chon SW, Rhim JW, Membrane J., 12, 255 (2002)
  •  
  • 16. Gholap SG, Jog JP, Badiger MV, Polymer, 45(17), 5863 (2004)
  •  
  • 17. Vauclair C, Tarjus H, Schaetzel P, J. Membr. Sci., 125(2), 293 (1997)
  •  
  • 18. Wang HH, Shyr TW, Hu MS, J. Appl. Polym. Sci., 73(11), 2219 (1999)
  •  
  • 19. Mitsushiro S, Hiroyuki Y, Hidenobu K, Shunji N, Polymer, 29, 2066 (1988)
  •  
  • 20. Karayiannis NC, Mavrantzas VG, Theodorou DN, Macromolecules, 37(8), 2978 (2004)
  •  
  • 21. Jang J, Lee DK, Polymer, 45, 1599 (2004)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2006; 30(4): 298-304

    Published online Jul 25, 2006

  • Received on Feb 14, 2006
  • Accepted on Jul 7, 2006