  • Preparation and Photoluminescence Characteristics of Liquid Silicone Rubber Containing Cadmium Selenide Nanoparticles
  • Kang DW, Lee BC, Kim JY
  • Cadmium Selenide Nanoparticles을 함유하는 액상실리콘 고무의 제조와 형광특성
  • 강두환, 이병철, 김지영
Abstract
Poly[(dimethylmethylvinyl)siloxane]phosphineoxide (PMViSPO) was prepared by adding phosphorus oxychloride (POCl3) to poly(dimethylmethylvinyl)siloxane (PMViS) at 0 ℃ under nitrogen atmosphere. Cadmium selenide (CdSe) was prepared by reacting cadmium oxide (CdO), tetradecylphosphonic acid (TDPA), trioctylphosphine oxide (TOPO) at 300 ℃, and adding solution of dissolved Se to tributylphosphine (TBP) and trioctylphosphine (TOP). CdSe-poly[(dimethylmethylvinyl) siloxane] phosphine-oxide (CdSe-SPO) adduct was synthesised by adding PMViSPO to CdSe solution. Liquid silicone rubber composite (LSRC-1) was prepared by compounding α,ω-vinyl poly(dimethylsiloxane)(VPMS), α,ω-hydrogen poly(dimethylsiloxane)(HPMS), and CdSe under Pt catalyst, and also LSRC-2 was prepared from VPMS, HPMS, and CdSe-SPO using Pt catalyst. It was confirmed that CdSe nanoparticles with photoluminescence characteristics was dispersed uniformly in LSR matrix. The diameter of CdSe was 30∼50 nm. By measuring the number of CdSe nanoparticles, 202 particles of CdSe in LSRC-2 and 166 particles of CdSe in LSRC-1 were dispersed in the same area of LSR matrix. Thermal stability for LSRC-2 compounded with CdSe-SPO was better than LSRC-1.

Poly[(dimethylmethylvinyl)siloxane 공중합체(PMViS)를 phosphorus oxychloride(POCl3)와 반응시켜 poly[(dimethylmethylvinyl)siloxane]phosphine oxides(PMViSPO)를 제조하였다. Cadmium selenide (CdSe)는 cadmium oxide(CdO), tetradecylphosphonic acid(TDPA), trioctylphosphine oxide(TOPO)를 300 ℃에서 반응시키고 여기에 Se를 용해시킨 tributylphosphine(TBP)과 trioctylphosphine(TOP)을 가한 다음 320 ℃에서 반응시켜 제조하였다. 또한 CdSe 제조 용액에 PMViSPO를 가하여 CdSe-SPO adduct를 제조하였다. 백금 촉매 존재 하에서 α,ω-vinyl poly(dimethylsiloxane)(VPMS), HPMS, CdSe 또는 CdSe-SPO를 고속 교반기에 취하고 컴파운딩하여 CdSe 함유 액상실리콘 고무 composite(LSRC-1)와 CdSe-SPO 함유 LSR composite(LSRC-2)를 제조하였다. 제조한 LSR composites 내에 함유된 형광 물질인 CdSe nanoparticles의 분산형태를 측정하여 입자 크기가 30∼50 nm인 입자가 균일하게 분포되어 있음을 확인하였고 LSRC-2의 분산도가 LSRC-1보다 우수함을 확인하였다. 또한 CdSe 입자의 개수를 측정한 결과 동일한 면적에 대하여 166개와 202개로 보다 많은 개수의 CdSe가 LSRC-2에 함유됨을 알 수 있었다. LSR composites의 열적 특성을 측정한 결과 CdSe-SPO가 함유된 LSRC-2의 열안정성이 높게 나타났다.

Keywords: poly[(dimethylmethylvinyl)siloxane]phosphineoxide; cadmium selenide; CdSe-poly[(dimethylmethylvinyl)siloxane]phosphineoxide; liquid silicone rubber; photoluminescence

References
  • 1. Choi HK, Yoon T, Prospect. Ind. Chem., 2(4), 41 (1999)
  •  
  • 2. Khun MSKorea Pat., 072659 (1998)
  •  
  • 3. Kang DW, Lee KS, Yeo HG, Shim JS, J. Korean Ind. Eng. Chem., 13(6), 594 (2002)
  •  
  • 4. Jones RG, Ando W, Chojnowski JSilicon-Containing Polymers, Kluwer Academic Publishers, Dordrecht, Netherlands (2000)
  •  
  • 5. Steigerwald ML, Alivisatos AP, Gibson JM, Harris TD, Kortan R, Muller AP, Thayer AM, Duncan TM, Douglass DC, Brus LE, J. Am. Chem. Soc., 110, 3046 (1988)
  •  
  • 6. Alivisatos AP, Science, 271(5251), 933 (1996)
  •  
  • 7. Peng XG, Manna L, Yang WD, Wickham J, Scher E, Kadavanich A, Alivisatos AP, Nature, 404(6773), 59 (2000)
  •  
  • 8. Murray CB, Norris DJ, Bawendi MG, J. Am. Chem. Soc., 115, 8706 (1993)
  •  
  • 9. Wang WZ, Geng Y, Yan P, Liu FY, Xie Y, Qian YT, J. Am. Chem. Soc., 121(16), 4062 (1999)
  •  
  • 10. Peng ZA, Peng XG, J. Am. Chem. Soc., 123(1), 183 (2001)
  •  
  • 11. Peng ZA, Peng XG, J. Am. Chem. Soc., 123(7), 1389 (2001)
  •  
  • 12. Kang DW, Kim JY, J. Ind. Eng. Chem.submitted (2006)
  •  
  • 13. Manna L, Scher EC, Alivisatos AP, J. Am. Chem. Soc., 122(51), 12700 (2000)
  •  
  • 14. Xu L, Chen K, El-Khair HM, Li M, Huang X, Appl. Surf. Sci., 172, 84 (2001)
  •  
  • 15. Skaff H, Ilker MF, Coughlin EB, Emrick T, J. Am. Chem. Soc., 124(20), 5729 (2002)
  •  
  • 16. Dabbousi BO, Rodriguezviejo J, Mikulec FV, Heine JR, Mattoussi H, Ober R, Jensen KF, Bawendi MG, J. Phys. Chem. B, 101(46), 9463 (1997)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2006; 30(3): 266-270

    Published online May 25, 2006

  • Received on Feb 23, 2006
  • Accepted on May 18, 2006