The applications of dental restorative composite resins containing 2,2-bis [4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane as a base resin, and triethylene glycol dimethacrylate, as a diluent, were often limited in dentistry due to the relatively large amount of volumetric shrinkage that occurs during the curing reaction. In this study, in order to reduce volumetric shrinkage of the current dental restorative composite resin, asymmetric spiro orthocarbonates were synthesized and then the characteristics of resin composites containing them were explored. The volumetric shrinkage of the dental composites containing spiro orthocarbonates was decreased approximately 45%. However, the curing characteristics and mechanical properties of the new dental composites were slightly poor than those of the commercially available dental composite.

2,2 bis [4-(2-hydroxy-3-methacryloyloxypropoxy)phenyl]propane을 기본 단량체, triethylene glycol dimethacrylate를 희석제로 포함하고 있는 고분자계 치아 수복재는 중합 수축률에서의 문제점으로 인하여 사용에 제약을 받아오고 있다. 본 연구에서는 기존 고분자계 치아 수복제의 문제점인 중합 수축률을 감소시키기 위해 중합시 부피 팽창이 기대되는 비대칭 스파이로 오쏘카보네이트를 합성하고, 이를 포함하는 새로운 치아 수복재를 제조하여 이의 특성을 시험하였다. 스파이로 오쏘카보네이트를 포함하는 새로운 치아 수복재의 중합 수축율은 약 45% 감소하여 우수한 체적 안정성을 나타내었다. 그러나 새로운 치아 수복재의 중합 특성, 기계적 물성 등은 기존 치아 수복재에 비해 다소 저하되었다.

Keywords: dental composite; resin matrix; asymmetric spiro orthocarbonates; volumetric shrinkage