  • Microporous Hollow Fiber Membrane Prepared from High Density Polyethylene/Ultra High Molecular Weight Polyethylene Blend
  • Nam JY, Choi SE, Lee KH, Jang MS, Kim JH, Lim SH
  • 고밀도 폴리에틸렌/초고분자량 폴리에틸렌 블렌드로 제조한 미세다공성 중공사막
  • 남주영, 최승은, 이광희, 장문석, 김진호, 임순호
Abstract
Hollow fiber was prepared from the blend of a high density polyethylene (HDPE)/ultra high molecular weight polyethylene (UHMWPE). The changes in the morphology and mechanical property of the hollow fiber were investigated. The commercial product (Sterapore), having a high water permeability, was analyzed with viscosity measurement and FT-IR. The molecular weight of Sterapore was very high and its surface was coated with a vinyl alcohol/vinyl acetate copolymer. the content of UHMWPE in the HDPE/UHMWPE blend was limited below 10 wt%. In order to improve the dispersion of UHMWPE, a mineral oil should be introduced in the blend. The morphology and mechanical property of the hollow fiber of HDPE/UHMWPE blend were similar to those of the commercial product.

고밀도 폴리에틸렌 (HDPE)과 초고분자량 폴리에틸렌 (UHMWPE)을 혼합하여 중공사막을 제조하고, 이의 형태구조와 물성 변화를 조사하였다. 분자량 측정과 FT-IR을 이용한 분석 결과, 상품화된 중공사막(Sterapore)은 고분자량의 HDPE로 제조되었으며, 표면은 친수성 고분자인 비닐 알코올/비닐 아세테이트 공중합체로 코팅되어 높은 수투과도를 갖는 이유를 규명하였다. HDPE/UHMWPE 블렌드에서 UHMWPE의 혼합 한계 조성비는 10 wt% 이하이며, UHMWPE의 분산성을 높이기 위하여 혼합과정에서 광유를 도입하여야 할 것으로 판단되었다. 제조된 HDPE/UHMWPE 블렌드 중공사의 기계적 물성과 막 구조는 Sterapore와 유사하였다.

Keywords: HDPE/UHMWPE blend; water permeability; hollow fiber

References
  • 1. Valdes F, Harasaki H, Meserko J, Kambic H, Malchesky P, Golding L, Nose Y, Trans. Am. Soc. Artif. Int. Org., 27, 270 (1981)
  •  
  • 2. Mizuo Shindo (Mitsubishi Rayon Co.), U.S. Patent, 4,530,809 (1985)
  •  
  • 3. Kensuke Kamada (Mitsubishi Rayon Co.), U.S. Patent, 4,055,696 (1977)
  •  
  • 4. Keller A, Marchin MJ, J. Macromol. Sci.-Phys., B1, 41 (1967)
  •  
  • 5. Tagawa T, Ogura K, J. Polym. Sci. B: Polym. Phys., 18, 971 (1980)
  •  
  • 6. Caron SL, J. Polym. Sci. Macromol. Rev., 11, 209 (1976)
  •  
  • 7. Cayrol B, J. Polym. Sci. B: Polym. Phys., 12, 2169 (1974)
  •  
  • 8. Sarada T, Sawyer LC, Ostler MI, J. Membr. Sci., 19, 97 (1983)
  •  
  • 9. Sprague BS, J. Macromol. Sci.-Phys., B8, 157 (1973)
  •  
  • 10. Japanese Patent Laid-Open No. 153872 (1979)
  •  
  • 11. Japanese Patent Laid-Open No. 38333 (1981)
  •  
  • 12. Jun Kamo U.S. Patent, 5,294,338 (1994)
  •  
  • 13. Wu QY, Wang X, Gao WP, Hu YL, Qi ZN, J. Appl. Polym. Sci., 80(12), 2154 (2001)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2003; 27(4): 307-312

    Published online Jul 25, 2003

  • Received on Dec 17, 2002
  • Accepted on May 20, 2003