  • A Study on Solution Blend of Poly(vinyl chloride) with Poly(VC-co-AN)
  • Lee S, Oh GS, Kim SR, Oh YS
  • 폴리 염화비닐(PVC)/염화비닐-아크릴로니크릴 공중합체의 용액 블렌드에 관한 연구
  • 이수, 오강석, 김성룡, 오영세
Abstract
Poly(vinyl chloride) was blended with vinyl chloride-acrylonitrile copolymers (MO-01 : Mw=199049, AN=22.79%, MO-02 : Mw=238523, AN=47.03%, MO-03 : Mw=289496, AN=52.49%, MO-04 : Mw=341837, AN=58.68%) by mixing dimethylformamide (DMF) solution of each polymer and their morphology, viscosity, viscoelastic and mechanical properties were studied. Blends of PVC and MO-01 showed a homogeneous morphology. On the contrary, the other copolymer blends showed a large phase separation with spherical domains. Miscibility of blends of PVC and MO-01 was shown to be better than that of blends of other copolymers from morphological and viscoelastic studies. Even though blends of PVC and MO-01 were observed to be the considerable compatibility at a composition of PVC/MO-01=90/10, the mechanical properties of blend films were not improved too much in most blend cases.

Poly (vinyl chloride) (PVC)와 vinyl chloride(VC)/acrylonitrile(AN) 함량비에 따른 poly(VC-co-AN)와의 블렌드 필름을 제조하여 morphology, 점도, 동적 점탄성 및 기계적 물성을 고찰하였다. 블렌드의 morphology는 전반적으로 matrix-domain 형태의 비상용계로 공중합체에서 VC 함량이 증가할수록 morphology는 다소 균일하였다. 특히 VC 함량이 77.21%인 MO-01 블렌드의 경우 PVC가 많은 영역에서 상용성은 우수하였다. 블렌드 용액의 점도는 전반적으로 비상용성으로 인하여 negative deviation을 보이나, MO-01 블렌드에서 PVC 함량이 90%일 때 급격한 점도의 증가를 보였으며, 저장탄성율 및 Tg 거동에서 MO-01 블렌드의 경우 상용성 블렌드의 Tg 변화와 경향이 유사하였으나 MO-02 및 MO-03의 경우 비상용성 블렌드의 경향을 나타내었다. PVC와 poly(VC-co-AN)의 블렌드에서 VC의 함량이 가장 높은 MO-01와 90:10인 조건에서의 상용성이 가장 뛰어났으며, 블렌드 필름의 기계적 물성의 향상은 발견할 수 없었다.

Keywords: blend; PVC; copolymer; morphology; viscoelastic property; compatibility

References
  • 1. Kim WS, Kim IH, Kang SC, Mori T, Tsuda Y, Ha KR, Polym.(Korea), 25(4), 521 (2001)
  •  
  • 2. Lieberman EP, Off. Dig. Fed. Soc. Paint Technol., 34, 30 (1962)
  •  
  • 3. Garton A, Aubin M, Prudhomme RE, J. Polym. Sci., 21, 339 (1983)
  •  
  • 4. Vinogradov GV, Fikhman VD, Alekseyeva VM, Polym. Eng. Sci., 12, 317 (1972)
  •  
  • 5. Ledous C, De Vries AU.S. Patent, 3,673,167 (1972)
  •  
  • 6. Gord LMan-made Fibres, Science and Technology, ed. H.F. Mark, et al., Vol. 3, p. 327, Interscience, New York (1968)
  •  
  • 7. Oh YS, Kim SR, Lee S, Kim BK, J. Macromol. Sci.-Phys., B34(3), 205 (1995)
  •  
  • 8. Oh YS, Lee S, Min SK, Shin YJ, Kim BK, J. Appl. Polym. Sci., 64(10), 1937 (1997)
  •  
  • 9. Huelck V, Thomas DA, Sperling H, Macromolecules, 5, 348 (1972)
  •  
  • 10. Kim SC, Klempner D, Frisch KC, Frish HL, Ghiradella H, Polym. Eng. Sci.
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2002; 26(5): 559-567

    Published online Sep 25, 2002

  • Received on Mar 20, 2002
  • Accepted on Sep 10, 2002