Various chitosan-g-PVA copolymer of different degree of grafting percentage and crystallinity were prepared by grafting of water soluble poly(vinyl alcohol) (PVA) onto chitosan. The polymer matrix containing prednisolone was cast from the solution in 10% aqueous acetic acid. The drug release rate was studied under various condition. The drug release rate was decreased as the degree of crosslinking or the crystallinity of the matrix was increased. However the drug release rate was increased as the content of grafted PVA increased. The initial release amount and rate were controlled by changing the crosslinking density or the crystallinity of the copolymer matrix, while pH values did not bring an effect on.

친수성 고분자이고 결정성의 조절이 용이한 폴리비닐알콜(PVA)을 chitosan에 그라프트시 켜 chitosan-g-PVA 공중합체를 합성하였다. 이를 10%-아세트산에 녹인 후 prednisolone을 가하여 충분히 분산시킨 다음 캐스팅하여 상온에서 건조하여 고분자 매트릭스를 제조하였으며 여러 조건에 따른 약물방출거동을 조사하였다. Chitosan-g-PVA 공중합체를 약물 전달체로 사용하는 경우, glutaraldehyde에 의해 가교도가 증가될수록 prednisolone 약물방출속도가 지연되었으며 또한, 열처리에 의해 공중합체내의 결정화도가 중가되고, PVA의 그라프트율이 낮을수록 약물방출속도가 지연되었다. 따라서 약물전달체의 가교도와 열처리에 의한 결정화도의 조절에 의해 초기약물 방출량과 속도를 조절할 수 있었으며, 이는 pH의 변화에는 크게 영향받지 않음을 알 수 있었다.

Keywords: chitosan grafted poly(vinyl alcohol); prednisolone; polymer matrix; release rate of drug