Article
  • Study on the Miscibility of Polyurethane/Polycarbonate Binary Blends
  • Ahn TO, Jung SU, Jeong HM
  • 폴리우레탄/폴리카보네이트 블렌드의 상용성에 대한 연구
  • 안태완, 정순욱, 정한모
Abstract
Polyurethane (PU) was synthesized from 4,4'-diphenylmethane diisocyanate, 1,4-butanediol, and poly(ethylene adipate) or poly(butylene adipate) diol (Mn= 2000) as a soft segment by prepolymer method in N,N-dimethylformamide. Hard segment content of PU was varied from 24 to 100 wt%. The synthesized PU was blended with bisphenol-A polycarbon-ate (PC) from a solution by casting method. PU/PC blends exhibited either two or single phase behavior depending on temperature and duration time of annealing by a differential scanning calorimeter. Such a behavior was attributed to the transreaction between PU and PC, and was studied further by thermal analysis methods.

4,4'-Diphenylmethane diisocyanate, 1,4-butanediol, 및 poly(ethylene adipate) biol 또는 poly(butylene adipate) diol (Mn=2000)을 사용하고, N,N-dimethylformamide를 용매로 하여 2단계 중합법에 의해 hard segment 함량이 24∼100wt%인 폴리우레탄(PU)을 합성하였다. 합성된 PU를 용액 블렌드법으로 bisphenol-A polycarbonate(PC)와 블렌드하여 그 상용 거동을 고찰하였다. PU/PC 블렌드물은 시차열량분석 시의 용융 온도 잊 가열 시간에 따라 단일상 또는 두 개의 상을 가지는 거동을 나타내었다. 이와 같은 거동의 이유는 PU와 PC간에 교환 반응이 일어나기 때문으로 판단되었고, 그 거동을 열분석 방법에 의해 관찰하였다.

Keywords: polyurethane; polycarbonate; miscibility; transreaction

References
  • 1. Brydson JAPlastics Materials, 5ed., p. 530, Butterworths, London (1989)
  •  
  • 2. Richardson TLIndustrial Plastics, p. 166, Delmar, New York (1989)
  •  
  • 3. Honma S, Kino Zairyo, Jan., 40 (1988)
  •  
  • 4. Takashi I, Kino Zairyo, Jan., 5 (1988)
  •  
  • 5. Bonk HWReaction Polymers, W.F. Gum, W. Riese. K, and H. Ulrich, eds., p. 279, Hanser, New York (1992)
  •  
  • 6. Goyert WU.S. Patent, 4,342,847 (1982)
  •  
  • 7. Skochdopole REU.S. Patent, 4,912,177 (1990)
  •  
  • 8. Goldblum KBU.S. Patent, 3,431,224 (1969)
  •  
  • 9. Schmelzer HGU.S. Patent, 4,350,799 (1982)
  •  
  • 10. Boutni OMEur. Patent, 265,790 (1983)
  •  
  • 11. Eric C, Rubber World, 199(6), 30 (1989)
  •  
  • 12. Koberstein JT, Gancarz I, J. Polym. Sci. B: Polym. Phys., 24, 2487 (1986)
  •  
  • 13. Cruz CA, Paul DR, Barlow JW, J. Appl. Polym. Sci., 24, 2101 (1979)
  •  
  • 14. Cruz CA, Barlow JW, Paul DR, Macromolecules, 12, 726 (1979)
  •  
  • 15. Wahrmund DC, Paul DR, Barlow JW, J. Appl. Polym. Sci., 22, 2155 (1978)
  •  
  • 16. Cruz CA, paul DR, Barlow JW, J. Appl. Polym. Sci., 23, 589 (1979)
  •  
  • 17. Snell FD, Ettre LSEncyclopedia of Industrial Chemical Analysis, vol. 19, p. 285, Interscience, New York (1979)
  •  
  • 18. Brunnette CM, Hsu SL, MacKnight WJ, Macromolecules, 15, 71 (1982)
  •  
  • 19. Koberstein JT, Galambos AF, Macromolecules, 25, 5618 (1992)
  •  
  • 20. Li Y, Gao T, Liu J, Linliu K, Desper CR, Chu B, Macromolecules, 25, 7365 (1993)
  •  
  • 21. Koberstein JT, Gancarz I, J. Polym. Sci. B: Polym. Phys., 24, 2487 (1986)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1995; 19(5): 606-614

    Published online Sep 25, 1995