Very low density polyethylene(VLDPE) and high density polyethylene-g-maleic anhydride(HDPE-g-MAH) grafted in molten state were melt blended in mixer. It's blend films were prepared to investigate the thermal and mechanical properties with VLDPE content. HDPE/VLDPE blends were also prepared to compare with the physical properties of HDPE-g-MAH/VLDPE blends. The single melting temperature was obtained regardless of VLDPE content in these blends and it increased with increasing HDPE-g-MAH content. On the whole, the % crystallinity and tensile modulus decreased with increasing VLDPE content, but the synergistic effect in tensile strength was shown in HDPE-g-MAH/VLDPE 80/20. The lmpact strength of these blends increased with increasing VLDPE content.

Dicumyl peroxide를 개시제로 사용하여 혼합기내에서 용융상의 고밀도 폴리에틸렌(HDPE)과 무수말레인산(MAH)을 그라프트 공중합시키고, 미반응 MAH는 아세톤으로 제거하였다. 이렇게 하여 얻은 HDPE-g-MAH를 초저밀도 폴리에틸렌(VLDPE)라 용융 블렌드하고, VLDPE의 조성비에 따른 열적, 기계적 특성을 측정하였다. 그리고 MAH의 그라프트 공중합에 따른 블렌드의 상용성의 변화를 조사하기 위하여 HDPE-g-MAH/VLDPE 블렌드의 물리적 특성을 HDPE/VLDPE 블렌드의 것과 비교하였다. HDPE-g-MAH/VLDPE와 HDPE/VLDPE 블렌드는 VLDPE의 조성비에 관계없이 단일융점을 나타내었다. 이들 두 블렌드의 결정화도와 인장 탄성률은 VLDPE의 조성비가 증가함에 따라 감소하였다. 그러나 HDPE-g-MAH/VLDPE 80/20에서 상승효과에 의해 가장 우수한 인장강도를 얻었다. 또한 이들 두 블렌드의 내충격강도는 인성이 우수한 VLDPE의 조성비가 증가함에 따라 급격히 증가하였다.

Keywords: Polyethylene; blends; maleic anhydride; tensile strength; impact strength