SBS triblock copolymer was functionalized with maleic anhydride(MA) using dicumyl peroxide (DCP) as an initiator. Functionalized rubber was blended with nylon6 in a twin screw extruder to prepare toughened nylon. DCP amount was fixed as 0.3 part. MA amount was varied from 0.5 to 2 parts of the rubber by weight. Different amounts of functionalized rubbers were blended with nylon6. Thermal, rheological and mechanical (tensile strength) properties of the blends were investigated. The crosslinking effect of the rubber on tensile strength of the blends was also investigated. Unlike crosslinking effect on tensile strength of the single phase, remarkable change was not noticed in the toughened nylon. General behaviour of the toughened nylon was changed with the elastomer's dispersion state.

SBS 트리블록공중합체를 dicumyl peroxide(DCP)를 개시제로 사용하여 maleic anhydride(MA)와 반응시킨후 나일론6와 이축혼련기내에서 혼합하여 강화된 나일론을 제조하였다. DCP의 양을 고정시키고 MA를 변화시켜서 서로 다른 정도로 기능화 된 SBS고무가 나일론에 첨가되었을 때 이들이 블렌드의 열적, 유변학적 성질 및 인장강도에 미치는 영향을 살펴보았다. MA가 첨가되었을 때 실제로는 부가반응이외에 서로 다른 분자의 디엔의 이중결합간에 반응하여 가교반응을 일으키므로 기능화 된 고무의 성질은 가교반응의 정도에 따라서 다르게 나타났다. 그러나 단일상내에서 가교반응이 진행되어 나타나는 기계적성질의 변화와는 달리 가교 된 고무의 블렌드 인장강도에 대한 영향은 그리 크지 않았다. 나일론6와 고무와의 전반적인 거동은 고무의 분산 상태에 따라서 변화하였다.