Wholly aromatic copolyesters were synthesized by melt polycondensation from phenylhydroquinone, 2, 8-naphthalene dicarboxylic acid p, p''-biphenyldicarboxylic acid, and their thermal properties were investigated by using DSC, polarizing microscope, TGA and TMA. The fiber molphology of the copolyesters was observed by using SEM and X-ray diffractometer, and fiber mechanical properties were investigated by Instron. These copolyesters formed turbid melts that showed strong stir-opalescence and nematic texture at the broad anisotropic region. The change of the solid-nematic transitions according to the copolymer compositions showed a eutectic point in the vicinty of the biphenyl content of 40wt%, but the isotropic transition point could not be seen up to 330℃. All of the copolyesters exhibited good spinability in anisotropic phase and their fiber''s morphology was fibrillar structure, and good mechanical properties in tensile test.

페닐하이드로퀴논에 바이페닐 디카르복실산과 나프탈렌디카르복실산을 적절한 몰비로 하여 용융중축합에 의해 전방향족 공중합 폴리에스테르를 합성하였다. 이들의 열적성질을 열시차분석, 열중량분석, 열기계분석으로 조사하였으며 액정구조를 편광현미경으로 관찰하였다. 또한 이들의 중합물을 용융방사한 후, X선회절 및 주사전자현미경을 이용하여 섬유의 결정정도와 미세구조를 관찰하였으며 인스트론을 이용 섬유의 기계적 성질을 조사하였다. 이들 공중합물의 액정발현 온도는 단독중합물 보다 낮았으며 PHNB 40일 때 275℃로 공중합물 중 가장 낮았으며 단독중합물 보다 약 100℃가량의 전이온도 저하가 발생하였다. 대부분 공중합물들은 섬유형성능이 좋았으며 섬유의 구조는 미세한 침상 피브릴 혹은 테이프 형태로 나타났으며 단독중합물 보다 결정형성능은 저하되었으나 섬유의 기계적 성질은 다소 우수한 것으로 판단된다.

Keywords: