  • Stress Relaxation Behavior of Particulates Filled Polypropylene
  • Choi KS, Kim CK
  • 무기입자 충전 폴리프로필렌의 응력완화 거동에 관한 연구
  • 최규석, 김척기
Abstract
An Experimental study was carried out to investigate the stress relaxation behavior of particulates (Perlite, CaCO3) filled Polypropylene. In order to improve the effect of interfacial adhesion, PP was melt-extruded with filler which was treated with acrylic acid (AA), in the presence of radical initiator, BPO. By this method, PP was grafted with AA which was treated onto filler. Stress relaxation modulus of treated composite was higher than that of untreated one. This result was greater at high temperatures particularly. Relaxation spectrum was described from stress relaxation behavior. Its shape was not clearly described by wedge type distribution or box type distribution but it was between the shape of a crystalline polymer and that of a rubber.

폴리프로필렌을 matrix polymer로 하고 성분과 형상이 다른 무기입자 즉 판상인 perlite, 입상인 CaCO3에 acrylic acid를 graftomer로 하여 표면처리하여 제조한 composite과 미처리하여 제조한 composite에 대한 응력완화거동을 -25℃에서 85℃ 사이에서 각각의 충전물에 대하여 실험하였다. 이 실험결과를 토대로 합성곡선(master curve)과 응력완화 스펙트럼을 작성하여 각각의 충전물에 대하여 처리시와 미처리시를 비교하여 보았다. 그 결과 응력완화 탄성률은 충전계가 matrix PP보다 상승 하였으며 충전계에 있어서는 처리시가 미처리시보다 크게 나타나고 있었다. 특히 고온에서 처리효과가 크게 나타남을 알 수 있었다. 응력완화거동으로부터 완화스펙트럼을 작성하였으며 그모양은 wedge type distribution이나 box type distribution을 확실하게 나타내고 있지 않으나 부분가교고무의 형상과 결정성 폴리머의 형상 중간에 위치함을 알 수 있었다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1989; 13(5): 426-432

    Published online Jun 25, 1989

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: