  • Polymerization of Propylene with High-Activity Catalysts : Ⅱ. Effect of Polymerization Conditions
  • Lee DH, Min KE, Jo WH, Jeong YT
  • 고활성 촉매를 사용한 프로필렌 중합: Ⅱ. 중합조건의 영향
  • 이동호, 민경은, 조원형, 정영태
Abstract
The polymerization of propylene with MgCl2/TiC14 -TEA system in hexane has been studied in which the supporter MgCl2 has been treated by precipitation method. The effect of aging time, catalysts concentration ratio, concentration of external Lewis base and polymerization temperature on the yield. isotacticity and molecular weight of polypropylene has been investigated. This catalyst system showed maximum activity for [Al]/[Ti] ratio of ∼40 and at 50℃ of polymerization temperature. In the case of absence of internal Lewis base, the catalyst system required the aging time. whereas the aging time was not necessary for the presence of internal Lewis base. It was also found that, with an increase of external Lewis bate the yield and molecular weight of isotactic polymer increased. whereas the yield of atactic polymer decreased very sharply, which consequently caused the enhance of stereospecificity and the decrease of total yield.

지지제인 염화마그네슘을 침전법으로 처리하여 사염화티탄과 반응시켜 얻은 고활성 촉매로 프로필렌을 중합할 때에 촉매 성분의 숙성시간, 유기알루미늄화합물의 종류 및 농도, 외부 Lewis염기의 농도, 중합온도 등이 촉매의 활성과 입체규칙성 및 분자량에 미치는 영향을 연구하였다. 그리고 생성된 중합체의 형태도 전사현미경으로 조사하였다. 이 촉매계에서는 촉매성분의 농도비에 따라 최적조건이 존재하였으며, 최적농도비는 [Al]/[Ti]=40 부근에서 나타났다. 중합온도는 50℃에서 최대활성을 나타내었으며, 내부 Lewis 염기가 존재하지 않는 경우는 촉매성분 간의 숙성시간이 필요하였으나, 내부 Lewis 염기가 존재하는 경우는 숙성시간이 필요하지 않았다. 또 외부 Lewis염기의 농도가 증가함에 따라 촉매의 활성은 감소하였으나 입체규칙성과 분자량은 증가하였다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1989; 13(1): 68-75

    Published online Jan 25, 1989

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: