This study concentrates on the mechanical behavior and the matrix cracking development in the early fatigue and fatigue-creep life in cross-ply graphite/epoxy laminates T300/5208, (0°/90°)_2S. The replication technique was used to observe the transversal crack density variation for several loading levels. The life time was measured only for tole high load level. At this level, the creep has no effect on the number of cycles to failure. The longitudinal behalf·iota was slightly influenered by the creep interruption. This fact can be attributed to the fibre dominated longitudinal behavior in this system. And the transversal crack density in fatigue-creep is higher than that in fatigue loading. It comes from the higher load level in fatigue-creep than that in fatigue.

본 연구에서는 cross-ply carbon/epoxy laminate, T300/5208, (0°/90°)_2S의 fatigue와 fatigue-creep 하에서의 기동을 살펴 보았다. Replication technique을 사용하며, 하중이 비교적 낮은 경우의 초기상태에서, 매트릭스의 축방향에 수직인 crack들의 density 변화를 측정한 결과, fatigue-creep 에서의 crack density가 fatigue의 경우보다 높았다. 이는 fatiguecreep 에서의 평균 하중치가 fatigue의 경우보다 높음에 기인한다. 한편, 가해진 하중이 비교적 큰 경우, 즉, 매트릭스의 손상이 심한 경우에 fatigue-creep의 축방항 변형은 fatigue의 경우보다 약간 작았다. 이는 creep period 하에서의 fiber-stiffening 현상에 기인하다고 여겨진다. 그러나, 하중이 매우 높은 경우에 creep은 fatigue-life에 영향을 미치지 않았다. 이는 보강섬유와 매트릭스의 damage가 동시에 최종 파괴에 영향을 미치기 때문인 것으로 사료된다.

Keywords: