Ju-Hong Lee , Ju-Won Kim, Won-Bin Lim, Jin-Gyu Min, Ji-Hong Bae†
, and PilHo Huh†
School of Polymer Science & Engineering, Pusan National University, Busan 46241, Korea
부산대학교 응용화학공학부
Reproduction, stored in a retrieval system, or transmitted in any form of any part of this publication is permitted only by written permission from the Polymer Society of Korea.
A novel polymer binder with excellent mechanical properties was synthesized by blending polymethyl methacrylate (PMMA) and urethane acrylate (UA). As a result of comparing the mechanical properties according to the type and content ratio of polyol, it was confirmed that shear adhesion and transmittance were improved when 5 wt% of UA was mixed. The cross-linking point and amorphous region increased through the mixing of PMMA and UA. As a result of spectrophotometer (UV-vis) measurement, the transmittance increased to 94% in the visible ray region of 370 nm. In addition, through universal testing machine (UTM) measurement it was confirmed that the tensile strength increased by 30% and the elongation by 16% at the UA content of 5 wt%. The application of UA is expected to be a promising technology to be applied to the field of transparent binders for road marking in the future.
폴리메틸메타아크릴레이트(PMMA)에 우레탄아크릴레이트(UA)가 혼합하여 우수한 기계적 특성을 가진 신규 고분자바인더를 합성하였다. UA를 구성하는 폴리올의 종류 및 함량비를 변경하여 기계적 특성변화 실험 결과, 5 wt% UA를 PMMA에 혼합하였을 때, 높은 전단접착강도, 투과율 등 바인더의 기계적 물성이 향상되는 것을 확인하였다. PMMA만으로 바인더를 구성한 경우 대비, 가교점 증가로 높은 가교도를 가진 구조를 가진 것을 확인하였으며, 분광광도계(UV-vis) 측정결과, 가시광선영역의 370 nm 부근에서 비결정성 영역이 증가하여 투과도가 94%까지 상승하는 결과를 확인하였다. 뿐만 아니라 만능재료시험기(UTM) 측정결과 UA 5 wt% 함량에서 인장강도 30%, 신율 16%의 증가폭을 확인함으로써 UA가 PMMA와 혼합됐을 경우 바인더의 물성향상을 확인하였다. UA 적용을 통해 고내구성 및 투과도 개선은 향후 노면표시용 투명 고분자 바인더 분야에 적용될 유망한 기술로 예상된다.
Keywords: urethane acrylate, multifunctional urethane acrylate, polymeric binder, high transmittance, adhesive.
2023; 47(3): 320-325
Published online May 25, 2023
School of Polymer Science & Engineering, Pusan National University, Busan 46241, Korea