  • Gas Permeation Characteristics of Polyurethane Membrane
  • Min DS, Lee KH, Kim KY
  • 폴리우레탄막의 기체투과
  • 민동선, 이규현, 김계용
Abstract
The transport behaviour of CO2, N2, and O2 through polyetherurethane membranes were studied at different pressure and temperature. The permeability (P) and diffusion coefficient (D) obtained by time-lag method were increased with increasing pressure, temperature and molecular weight of diol, in the order CO2>N2>O2. Jump lengths (λ) obtained from the activation energy of diffusion and the cohesive energy density of polyurethane were 50A°for PU-1 and 49A° for PU-2. The entropy of activation (ΔS#) for diffusion was negative indicating that the dipolar interaction between Permeant and membrane was small, but the flexibility of soft segment in polyurethane was large.

폴리우레탄막의 기체투과특성을 검토하기 위하여 CO2, O2 및 N2기체를 사용하여 투과시험을 실시하였다. 시험결과로부터 폴리에테르우레탄막의 기체투과는 압력, 온도 및 디올의 탄소수가 커짐에 따라 투과계수 P 및 광산계수 D가 증가됨을 알 수 있었으며 CO2>N2>O2순으로 P와 D가 증가되었다. 또한 기체가 막내를 광산하는 점프길이 λ(A°)은 PU-1의 경우 50A°, PU-2의 경우는 49A°이었으며 ΔS#는 CO2>N2>O2순으로 감소되었다. ΔS#값이 (-)값인 것으로 미루어 보아 폴리우레탄 막과 투과기체간의 쌍극자상호작용은 크지 않으며 우레탄내의 soft segment의 flexibility가 큼을 알 수 있었다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1983; 7(2): 96-102

    Published online Apr 25, 1983

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: