To modify the hydrophobic property of poly (ethylene terephthalate) (PET) fiber such hydrophilic monomers as acrylic acid (AA) , methacrylic acid(MAA), and AA/MAA mixture were grafted to PET. The grafting reactivity of commercial PET fiber was improved by swelling the fiber with 1,1,2,2-tetrachlorcethane. Benzoyl peroxide (BPO) was the initator for the two-step grafting. The first step was the pretreatment of PET with an emulsion of BPO and the second was the grafting of the pretreated PET in an aqueous monomer solution containing cupric sulfate as a homopolymerigation inhibitor. Diffusion of BPO into PET and decomposition of BPO during the pretreatment showed an opposite effect on the generation of the active species for grafting, and so the conditions of pretreatment on grafting was emphasized on these effects. The mixture of AA and MAA gave a higher grafting yield than each monomer alone, giving the maximum yield at the mole ratio of 2/3 in AA/MAA. The grafting improved the moisture retention and dyeability of PET fibers.

본 연구는 acrylic acid (AA), methacrylic acid(MAA) 및 AA/MAA 혼합물을 사용하여 그래프팅하므로써 poly(ethlylene terephthalate) (PET)의 소수성을 개질하는 것을 목적으로 하였다. 상용 PET 섬유는 그래프팅에 대해 반응성이 낮기 때문에 1,1,2,2-tetracholoroethane을 swelling agent로 사용하여 반응성을 향상시켰다. 2단계 그래프팅에 있어서 제 1단계는 개시제로 사용한 benzolyl peroxide(BPO)의 에멀젼으로 PET를 처리하는 것이고 제 2단계는 전처리된 PET를 homopolymer 생성억제제인 cupric sulfate가 포함된 monomer의 수용액체서 그래프팅하는 것이다. PET 내부로 BPO의 착산과 전처리 과정에서의 BPO의 분해가 그래프팅 활성에 상반된 영향을 주며 따라서 이러한 관점에서 그래프팅에 대한 전처리 조건의 영향이 연구되었다. AA와 MAA의 혼합물은 각각의 monomer보다 높은 그래프트율을 나타냈고 AA/MAA의 몰비가 2/3일 때 최고 그래프트율을 나타냈다. 그래프트된 PET는 흡습성과 염색성이 상당히 향상되었다.

Keywords: