Polymer/polyols were prepared by polymerizing vinyl monomers in the presence of poly(propylene glycol). Acrylonitrile, methyl methacrylate and styrene were used as vinyl monomers and 2, 2''-azobisisobutyronitrile was used as an initiator. The polymer/polyols thus obtained showed suspension of vinyl polymers in poly (propylene glycol). The suspension stability, particle size of the suspension and the presence of the graft copolymer were evaluated. Polymer/polyols made from acrylonitrile showed excellent suspension stability, but those made from the others showed phase separation over a period of from 1 to 2 weeks. In polymer/polyols made from acrylonitrile, the suspensible particles appeared to be generally uniform in size, with the ranges of 2-5 microns in diameter and the degree of polymerization of vinyl polymers and graft efficiency did not appear to vary appreciably with the vinyl concentration of up to 20%. Polyurethane elastomers based on polymer/polyols made from acrylonitrile had shown tensile strength, modulus, tear resistance and hardness superior to those made from poly (propylene glycol) alone, but elongation decreased as vinyl portion increased.

acrylonitrile, methyl methacrylate, styrene등의 비닐단량체를 poly (propylene glycol) 내에서 2, 2''-azobisisobutyro nitrile을 개시제로 사용하여 중합시켜, graft 공중합체를 함유하는 분산상의 polymer/polyol을 얻었다. 반응결과, acrylonitrile을 단량체로 사용한 경우, 매우 좋은 분산상태를 갖는 생성물을 얻을 수 있었으나, styrene이나 methyl methacrylate를 사용했을 때에는 분산안정도가 좋지 않아 상하로 상분리되는 현상을 보였다. acrylonitrile을 단량체로 사용하여 얻은 polymer/polyol에 있어서, 분산입자의 평균직경은 2∼5μ 정도 되었으며, 비닐성분의 함량이 증량분율로 20% 이하일 때, polyacrylonitrile 성분의 중합도 및 graft 효율등은 비닐함량의 변화에 따라 별로 차이를 보이지 않았다. 또한 이들을 원료로 하여 합성한 polyurethane 탄성체의 기계적성질에 있어서, 비닐함량이 증가에 따라 인장강도, 인열강도, 탄성율, 경도등은 점차 강화되었으나, 신장율은 감소하는 경향을 보였다.

Keywords: