The production rate of carbonyl groups on a LDPE film treated in an oxygen corona discharge shows faster increase than that of ethylenic double bonds to suggest that the corona oxidation follows closely a photo-oxidation mechanism. The formation of hydroperoxides regarded as the primary step in the production of other oxygen containing groups is confirmed in the oxygen corona treatment by detecting the appearance of a sulfate ester band in IR spectra after treatment of the oxidized film with SO₂ gas. The rate of oxidation by the oxygen corona process seems to be controlled by the rate of diffusion of some active species into the bulk of the polymer. In a short time of oxygen corona treatment, activation energy of the oxidation is 9.0 Kcal/mol; the value is in good agreement with the value obtained for ozone-oxidation of LDPE.

저밀도 폴리에틸렌 필름을 코로나방전으로 처리하면 카르보닐기의 농도가 이중결합 농도보다 빨리 증가하며 이 때의 산화기구는 광산화기구와 비슷하다. 방전처리된 물질을 아황산가스로 다시 처리하여 적외선 분광법으로 확인하면 다른 산화방법에 의해서 고분자물질에 생기는 초기 산화물인 과산화물질이 코로나 방전 처리에서도 생성됨을 알 수 있다. 산소코로나방전처리에 의하면 저밀도 폴리에틸렌의 산화속도는 산화성 물질이 고분자 물질속으로 확산해 들어가는 속도와 비슷하다. 짧은 방전처리시간 동안은 산화활성화 에너지는 9.0Kcal/mol이며 이 값은 오존에 의한 산화활성화 에너지와 거의 같다.

Keywords: