The optical properties and dimensional stability of polyethersulfone(PES) retardation film have been studied as function of chain orientation and the temperature applied to PES retardation film. It was confirmed that the appropriate retardation values of Re and Rth for the retardation film application were able to obtain by the chain orientation and these values could be controlled by the chain relaxation through the thermal annealing process. It was found that unstable Re and Rth values were shown by the repeated cooling and heating applied to the retardation films but this could be stabilized by means of the annealing process after stretching of PES film. The dimensional shrinkage due to the chain orientation was found as temperature increase and the intrinsic thermal expansion of PES appeared after shrinking. The shrinkage of PES films affected by the chain orientation and thermal annealing dramatically but the effect on the coefficient of thermal expansion was found to be negligible.

폴리에테르설폰(PES) 필름의 주사슬 연신에 의한 광학 특성 변화와 보상 필름으로 사용 환경온도에 따른 이들의 특성변화를 살펴보았다. 아울러 연신 및 열처리가 필름의 광학 특성 및 치수안정성에 미치는 영향을 함께 확인하였다. PES는 연신에 의하여 광학용 보상 필름으로 사용이 가능할 정도의 Re 값과 Rth 값을 얻을 수 있었으며 이러한 값들은 반복적인 사용 환경 온도에 따라 변화되며 이를 최소화하기 위하여 열처리 공정이 필요함을 알 수 있었다. 연신된 PES 필름은 사용온도가 증가됨에 따라 연신에 의한 주사슬의 수축이 발생되며 그 이후 고유 특성인 열팽창이 일어나며, 연신에 의한 주사슬 배향에 의하여 열팽창계수는 다소 감소함을 알 수 있었다. 필름의 열처리는 열팽창계수에는 크게 영향을 미치지 않는 반면 열수축을 현저하게 감소시킴을 확인하였다.

Keywords: polyethersulfone film; retardation film; coefficient of thermal expansion; dimensional stability