The structural development of triacetyl cellulose (TAC) was studied as a function of solution casting processing parameters such as dope concentration, evaporation temperature, annealing temperature and the addition of plasticizer. The crystalline structure was developed by the solution casting and the level of crystallinity was increased with increasing dope concentration and evaporation temperature. The crystalline structure could be enhanced by the annealing process after formation of TAC film. Introducing plasticizer resulted in decreasing melting temperature and crytallinity of TAC film due to the increase of chain mobility. It was also found that thermal stability of TAC was improved due to the rigid structure of applied plasticizer.

트리아세틸 셀룰로오스(triacetyl cellulose, TAC) 용액필름 가공 시, 가공 공정 변수인 TAC 도프(dope)의 농도, 용매 제거 온도, 열처리 온도와 흐름특성 증가를 위하여 사용되는 가소제의 첨가가 TAC 필름의 구조 변형에 미치는 영향을 살펴보았다. 사용 도프의 농도가 높을수록, 용매 제거 온도가 높을수록 TAC의 결정화가 더 잘 발현됨을 알 수 있으며 이러한 결정화는 TAC 필름의 제조 후 열처리에 의하여 증가됨을 확인하였다. 또한, 가소제의 첨가에 의한 주사슬의 유연성 증가에 의하여 용융온도 및 결정화도가 감소하며 첨가된 가소제의 방향족 구조로 인하여 필름의 열분해 안정성이 우수해짐을 알 수 있었다.

Keywords: triacetyl cellulose film; solution casting; crystalline structure; plasticizer