Major products obtained from pyrolysis of Teflon are C₂F₄, C₃F₆ and cyclo-C₄F₈ and mole percent distribution of each component varied with temperature, pressure and flow rate of inert carrier gas. Experiments were performed under five temperatures between 550 and 800℃ and seven pressures between 760 and 2mmHg. Experiments were also performed under same five temperatures and four flow rates of nitrogen carrier gas between 50 and 170 ml/min. Accumulation of C₂F₄ was facilitated by reducing the pressure or increasing the flow rate of nitrogen carrier gas. Raising the pyrolysis temperature facilitated C₂F₄ formation but diminished C₂F₄ formation. Cyclo-C₄F₈ was unstable at high temperatures and its amount sharply decreased at high temperatures. It was confirmed from the experimental results that pyrolysis of teflon occurred via formation of C₂F₄, which was further pyrolyzed to produce C₃F₆ and Cyclo-C₄F₈.

Teflon의 열분해에서 주요생성물로 C₂F₄, C₃F₆ 및 cyclic-C₄F₈를 얻었으며 열분해 조건에 대한 이들 생산물 분포의 변화를 알아 보았다. Carrier gas를 사용한 실험은 550∼800℃의 온도범위에서 질소의 유량을 50∼170ml/min로 변화시켜가며 하였으며 유량이 증가함에 따라 C₂F₄가 증가함을 알았다. 같은 온도범위내에서 압력을 대기압에서 진공까지 변화시켜가며 실험하여 압력이 낮아질수록 C₂F₄가 증가하고 C₃F₆, cyclic-C₄F₈가 감소함을 알았다. 모든 경우에 온도가 높아질수록 C₂F₄의 양은 감소하고 C₃F₆의 양은 증가하였다. Cylclic-C₄F₈는 고온에서 불안정하여 분해되므로 그 양이 급격히 감소한다. 실험결과로부터 Teflon의 열분해 mechanism은 고분자사슬에서 C₂F₄가 떨어져 나오며 그것이 다시 열분해하여 다른 생산물이 생긴다는 가정이 타당함을 알았다.

Keywords: