Polyaniline(PANi)/Poly(ethylen oxide)(PEO) in-situ vlends were prepared vby inducing phase separation through solvent evaporation after casting from solutions contnaing anline monomer, oxidant (initiator), dopant an PEO in methanol/water mixed solvent, It was observed that the electrical conductivity first increases rapidly as PANi amount in the PANi/PEO blend increases and then slowly increases as the weight percentages of polyaniline become above 11wt% in the blend. We also noted that the morphology of PANi/PEO blends changes when the holding time in a stirrer at constant temperature is varied and eventually affects the electrical conductivity. As the length of alkyl group in dopants indreases, the electrical conductivity of doped blends increases. The PANi/PEO blend prepared with a high molecular weight of PEO yields higher electrical conductivity.

메탄올/물의 혼합용매에 아닐린 단량체, 산화제, 도판트 그리고 PEO를 넣어 일정시간 교반한 후, 용액을 캐스팅하여 용매를 증발시켜 전도성 고분자인 폴리아닐린(PANi)과 열가소성 매트릭스 고분자인 폴리에틸렌옥사이드(PEO)가 혼합도니 블렌드를 얻었다. 블렌드 내의 중합된 PANi의 양이 많아질수록 전기전도도가 증가함을 알 수 있었고, PANi의 함휴량이 11wt%만 되어도 전기전도도가 약 0.15S/cm값을 나타내었다. 교반조 내의 체류시간에 따라 PANi/PEO 블렌드의 형태학이 변함을 관찰하였으며, 이러한 형태학이 전기전도도에 영향을 미침을 알았다. 또한 도판트의 분자크기가 커질수록 제조된 블렌드의 전기전도도가 증가함을 관찰하였다. 매트릭스 고분자로 사용된 PEO 분자량을 변화시키며 블렌드를 제조하였을 때, PEO의 분자량이 클수록 제조된 PANi/PEO블렌드의 전기전도도가 증가함을 관찰하였다.

Keywords: