Montmorillonite (MMT) was organically modified with dodecylammonium bromide (DA) to prepare the poly(ε-caprolactone) (PCL)/DA-MMT by melt intercalation at 80 ℃. X-ray diffraction (XRD) results showed that the intercalation of polymer chains led to an increase in the spacing between silicate layers (24.5 Å). However, the amount of PCL had no effect on the d-spacing of silicate layers. As th intercalation progressed, heat of fusion and melting point were reduced. It was found the well dispersed PCL/clay nanocomposites also can be obtained by mechanical mixing with two-roll mill at 150 ℃ fir 15 min, which was confirmed by XRD and TEM. For this nanocomposite, crystallization temperature and rate of crystallization of PCL were increased.

용융 삽입법으로 poly(ε-caprolactone) (PCL)을 모노릴로나이트 (MMT)에 삽입하기 위하여 도데실암모늄 브로마이드를 이용하여 몬모릴로나이트 내부를 개질한 후, PCL(10000)을 80 ℃에서 용융 삽입하였다. XRD의 결과로부터 실리케이트 층사이에 고분자가 삽입됨으로써 실리케이트의 d값이 증가하였음을 확인하였다 (24.5 A). 그러나 PCL의 양에 따른 실리케이트의 d값의 변화에는 아무런 영향이 없었으며, DSC로 과날한 결과, PCL이 몬모릴로나이트에 삽입이 진행됨에 따라 PCL의 용융열과 용융점이 감소하였다. 그리고 PCL이 삽입된 DA-MMT(PCL-MMT)와 PCL(80000)을 150 ℃에서 15분 동안 two-roll mill로 기계적으로 혼합하여 XRD와 TEM으로 관찰한 결과 PCL의 매트릭스에 실리케이트 층이 독립적으로 잘 분산되어 있는 PCL/clay 나노복합재료를 제조할 수 있었다. 나노복합재료일 경우

Keywords: PCL의 결정화 온도와 결정화 속도가 증가하였다.

Keywords: sodium montmorillonite; polycaprolactone; melt intercalation; nanocomposite