In this study, xerographic properties of double-layer photoconductor dopde with liquid crystals as charge-carrier transport material were investigated. The double-layer photoconductor consists of the nematic liquid crystals(5CT, 7CB, 80CB, and E7) doped with 2,4,7-trinitrofluorenone as a charge-carrier transport material and the metal-free phthalocyanine (H₂Pc) dispersed in polyvinylbutyral as a charge-carrier generation material. In the results of measured surface voltage properties for phtoconductor doped with liquied crystals, TNF : 5CT (40wt%) sample showed the lowest dark decay, the lowest residual voltage and the highest sensitivity among others because the molecular ordering of the liquid crystal enhanced charge-carrier trasport mobility.

유기 광도전체는 분자 배열이 불규칙한 비정성 고체계로서 charge-carrier 이동도가 무기 광도전체에 비해 매우 낮다. 유기 적층형 광도전체의 전하수송층에 액정 (5CT, 7CB, 80CB 및 E7)을 혼합시킴으로써, 광도전체에 있어서의 분자 배향이 charge-carrier 수송 특성에 어떠한 영향을 미치는지 관찰하였다. 액정을 혼합시켜 제작한 유기 광도전체는 액정의 농도비가 증가할수록 암감쇄는 거의 0에 가까웠다. 그리고 사용한 액정 가운데 5CTRp 액정이 가장 우수한 표면전위 특성을 나타내었다. 특히 2,4,7-trinitrofluorenone에 대해 40 wt%의 농도로 혼합하여 급냉시켜 제작한 5CT계 감광체는 암감쇄도 거의 일어나지 않았으며, 감도면에서도 우수한 값을 나타내었고, 잔류전위도 매우 작게 나타났다.

Keywords: photoconductor; carrier transport material; carrier generation material; xerographic property; liquid crystal