  • The Permeability of Solute through Chitosan-g-Poly(vinyl alcohol) Copolymer Membranes
  • Kweon DK, Kang DW, Oh SM
  • Chitosan-g-Poly(vinyl alcohol) 공중합체막의 용질 투과능에 관한 연구
  • 권동건, 강두환, 오수민
Abstract
By grafting PVA with easily controlled crystallinity and high mechanical properties onto chitosan which has an excellent biocompatibility, chitosan-g-PVA copolymer was prepared. And then copolymer membrane was prepared by solvent casting technique. The swelling ratio (Q) and permeability of riboflavin through the copolymer membranes decreased at pH 1.2, but increased at pH 7.4 with PVA grafting %. And also, permeability of the solute was controlled by changing the degree of crystallinity and crosslinking density of copolymer membrane.

생체적합성이 뛰어난 키토산에 결정성의 조절과 기계적 물성이 우수한 폴리비닐알콜(PVA)을 그라프트시켜 chitosan-g-PVA 공중합체를 합성한 후 이를 막으로 제조하여 여러 조건 변화에 따른 swelling ratio와 용질투과능 변화를 고찰하였다. Chitosan-g-PVA 공중합체막의 경우 pH 1.2에서는 PVA 그라프크율이 증가함에 따라 swelling ratio가 약간씩 감소하나 pH 7.4에서는 증가됨을 알 수 있었다. 모델약물로 riboflavin을 사용하는 경우, chitosan-g-PVA 공중합체막을 통한 용질 투과능은 pH 1.2에서는 PVA 그라프트율이 낮을수록, pH 7.4에서는 PVA 그라프트율이 높을수록 향상되었으며 또한 pH가 낮을수록 향상되었다. 그리고 열처리에 의해 공중합체 내의 PVA에 의한 결정화도를 증가시키거나 가교제 글루타알데히드에 의해 공

Keywords: chitosan-g-poly(vinyl alcohol) copolymer membrane; swelling ratio; riboflavin; lag time; permeability coefficient

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1998; 22(5): 749-755

    Published online Sep 25, 1998

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: