A montmorillonite-epoxy nanocomposite has been prepared by dispersing organically modified montmorillonite in an epoxy resin (diglycidyl ether of bisphenol A (DGEBA)) at elevated temperatures. Molecular dispersion of montmorillonite within the crosslinked epoxy matrix was verified using X-ray diffraction and transmission electron microscopy indicated that the final product contains a uniform dispersion of exfoliated 10 Å thin clay layers seperated by 100∼150Å of polyether polymer, thus verifying the nanocomposite structure. Differential scanning calorimetry studies of a nanocomposite containing 5wt% stearylammonium-montmorillonite indicated the heat of reaction and activation energy for the polymerization reaction to be 462 J/g and 98.2 kJ/mol, respectively.

스테아릴암모늄 브로마이드와 반응시킨 몬모릴로나이트를 에폭시수지 단량체(diglycidyl ether of bisphenol A (DGEBA))와 혼합한 후, 고온 경화 반응시켜 몬모릴로나이트-에폭시 나노복합재료를 합성하였다. 합성한 나노복합재료를 X-선 회절 실험과 투과전자현미경을 통하여 관찰한 결과 에폭시 매트릭스내에 몬모릴로나이트의 실리케이트층이 한층 한층 균일하게 분산되어 있음을 확인하였다. 그리고 각각의 층간거리는 100∼150Å정도였다. 열시차분석기를 이용하여 5 wt%의 스테아릴암모늄-몬모릴로나이트가 분산되어 있는 나노복합재료 합성시 중합열과 중합반응시 활성화 에너지를 확인한 결과 각각 462J/g과 98.2kJ/mol였다.

Keywords: nanocomposite; intercalation; exfoliation; montmorillonite; epoxy