Article
  • Synthesis of Reactive Microgels by Emulsion Copolymerization of Methyl Vinyl Ketone with Styrene and Their Reactivity
  • Park SW, Kim JS
  • 메틸비닐케톤·스티렌의 유화공중합에 의한 반응성 마이크로겔의 합성과 입자의 반응성
  • 박상원, 김정수
Abstract
Homopolymers of methyl vinyl ketone and its copolymers with styrene were prepared by the emulsion polymerization using divinylbenzene as a crosslinking agent. The quantitative effect of styrene and divinylbenzene on the colloidal stability, degree of crosslinking, and swelling ratio was investigated by measuring density and viscosity. The viscosities of latex particles decrease drastically with increase of crosslinking agent and content of styrene. The reactivity of particles was analysed by the product with hexamethylenediamine, of which -C = N- bonds were mostly observed in the condensation reaction between carbonyl and amino groups. The stability of the emulsion particles was maintained even after the reaction and the extent of reactions decreased with the crosslinker.

가교제로 디비닐벤젠을 사용하여 메틸비닐케톤의 단일중합체 혹은 스티렌과의 공중합체 입자를 유화중합에 의하여 합성하였다. 스티렌 및 디비닐벤젠의 량을 변화시킴으로써 이들이 콜로이드의 안정성, 가교도, 팽윤도에 미치는 영향을 밀도 및 점도 측정에 의하여 관찰하였다. 가교제의량이 증가함에 따라 입자의 점도가 급격히 감소하였고 검도의 감소효과는 스티렌의 량에 비례하였다. 입자의 반응성은 헥사메틸렌디아민과의 반응물을 분석하여 연구하였다. 화학결합은 주로 카보닐그룹과 아미노그룹의 축합에 의한 -C=N- 결합의 형성으로 관찰되었다. 반응후에도 에멀젼의 안전성이 유지되었으며 반응의 정도는 가교제의 량이 증가함에 따라 감소하였다.

Keywords: poly(methyl vinyl ketone); reactive microgel; particle viscosity; hexamethylenediamine

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1998; 22(1): 15-22

    Published online Jan 25, 1998

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: