Amidoximated chitosan bead-g-PAN copolymer was prepared by the reaction of cyano group of chitosan bead-g-PAN copolymer with hydroxylamine, after crosslinking of chitosan with glutaraldehyde and grafted AN. The metal ion adsorption percentage and the stability constant were measured under various conditions. The metal ion adsorption percentage for amidoximated chitosan bead-g-PAN copolymer(PAN grafting% : 170) decreased for Zn²⁺, Cd²⁺ and Hg²⁺, compared with that of crosslinked chitosan but increased for Cu²⁺, Mn²⁺. Specially, the adsorption percentage for Pb²⁺ was increased from 17.4% to 80.6% .The stability constants of amidoximated chitosan-g-PAN copolymer decreased from 15.56 to 15.20 for Zn²⁺, 15.56 to 14.41 for Cd²⁺, 20.07 to 20.02 for Hg²⁺, respectively. However those increased from 18.40 to 18.77 for Cu²⁺, 12.01 to 13.04 for Mn²⁺, 14.34 to 17.51 for Pb²⁺, compared with that of crosslinked chitosan.

가교 chitosan에 acrylonitrile (AN)을 그라프트시킨 후 이를 amidoxime화시켜 amidoxime화 chitosan bead-g-PAN 공중합체를 합성하였다. 이를 사용하여 여러 조건변화에 따른 여러 금속이온에 대한 흡착실험과 안정화도상수 변화를 살펴보았다. Zn²⁺, Cd²⁺, Hg²⁺의 경우 가교 chitosan에 비해 amidoxime화 chlitosan-g-PAN 공중합체 (PAN 그라프율:170)의 흡착율이 저하되는 반면에 Cu²⁺, Mn²⁺의 경우에 흡착율이 향상되었으며 특히 Pb²⁺의 경우 흡착율이 17.2%에서 80.6%로 매우 향상됨을 알 수 있었다. 또한 pH가 중가함에 따라 흡착능이 높아졌고, Cu²⁺, Pb²⁺는 다른 금속이온에 비해 amidoxime기에 대한 선택적 흡착능이 뛰어난 것으로 나타났다. 그리고 amidoxime화 chitosan bead-g-PAN 공중합체의 안정화도상수는 가교 chitosan에 비해 Zn²⁺는 15.56에서 15.20으로, Cd²⁺는 15.56에서 14.41로, Hg²⁺는 20.07에서 20.02로 다소 감소한 반면 Cu²⁺는 18.40에서 18.77로, Mn²⁺는 12.01에서 13.04로, Pb²⁺는 14.34에서 17.51로 향상됨을 알 수 있었다.

Keywords: amidoximated chitosan-g-PAN copolymer; adsorption percentage; selectivity; stability constant