In this study, the effects of a selected coupling agent on the electromagnetic and mechanical properties of an epoxy composite containing a Ni-Zn ferrite were investigated in terms of content of the coupling agent. The complex permeability, permittivity and electromagnetic attenuation value of the composite were obtained using an impedace/gain phase analyzer(HP4194A) and a network analyzer(HP8753C) in the frequency ranges from 1 MHz to 5 GHz. At a given frequency range, complex permeability, permittivity, and microwave absorbing attenuation of Ni-Zn ferrite/epoxy composite was constant with varying coupling agent amount. On the other hand, tensile strength and hardness value of the composite were greatly affected by the amount of the coupling agent ; the coupling agent treatment up to 1 ∼ 1.5 wt% improved the mechanical properties, however, the effect was saturated above this value. Therefore, without any detrimental effects of coupling agent on the electromagnetic properties at interested frequency range(1 ∼2 GHz), the mechanical properties could be optimized by addition of 1∼1.5 wt% of the coupling agent.

Ni-Zn 페라이트/에폭시 복합재료의 전자기적, 기계적 특성에 대한 결합제의 효과를 결합제의 함량에 따라 분석하였다. 복합재료의 복소 투자율과 유전율 및 전파 흡수 특성은 1 MHz에서 5 GHz의 주파수 영역에서 impedance/gain phase analyzer(HP4194A)와 network analyzer(HP8753C)을 이용하여 각각 구하였다. 에폭시-페라이트 복합재료의 복소 투자율과 유전율 및 전파 흡수 거동은 측정 주파수에서 결합제의 함량이 증가함에 따라 거의 일정한 값을 갖는다. 반면 기계적 특성의 경우 인장강도와 경도는 두 경우 모두, 결합제의 함량이 1∼1.5wt%까지는 함량이 증가함에 따라 증가하다가 그 이상의 함량에서는 거의 일정한 값을 갖는다. 그러므로 에폭시-페라이트 복합재료로 전파흡수체를 구현함에 있어서 적합한 결합제의 함량은 약 1∼1.5wt%이며, 결합제를 이 정도 양으로 첨가했을 경우 관심 주파수 대역(1∼2GHz)에서 전파 흡수 특성에도 영향을 미치지 않고 기계적 성질을 향상시킬 수 있다.

Keywords: electromagnetic absorber; attenuation; hardness; tensile strength; coupling agent