Two starch graft poly(methyl acrylate)s with different starch content and composition, the amylose content, were obtained by free radical copolymerization. Starch content in graft copolymer was determined by both side-chain separation and thermogravimetric analysis(TGA) methods. TGA method gave somewhat smaller values than side-chain separation method. However, TGA method was a faster and more convenient means for determining the level of starch in graft copolymer than side-chain separation. TGA data showed that starch content in graft copolymer after enzyme test for 10days was reduced to about 70 percents of original starch in graft copolymer. When copolymer films were stored under the circumstances of high relative humidity, tensile properties were reduced, which was due to the plasticizing action of water molecules in film. Crystallinities of copolymer films were also gradually disappeared. Water molecules swelled amorphous region and then destructed relatively unstable crystalline region in copolymer films. Tensile properties of S-g-PMA films were dependant on starch content and starch composition(the ratio of amylose vs. amylopectin). Graft copolymer with higher content of flexible, rubbery PMA and soft, linear amylose, showed lower tensile strength and higher elongation at break point.

자유라디칼 공중합반응에 의해 전분의 함량 및 전분의 조성(아밀로스와 아밀로펙틴의 비)이 다른 두종의 전분 그라프트 폴리메틸아크릴레이트(S-g-PMA)를 제조하였다. 공중합체내의 전분의 함량을 side-chain separation 방법 과 thermogravimetric analysis(TGA) 방법을 이용하여 측정 하였다. TGA 방법에 의한 측정치는 side-chain separation 방법보다 다소 작았지만 그라프트 공중합체내의 전분함량을 측정하는데 보다 빠르고 편리한 방법이었다. TGA 방법에 의해 10일간 효소시험한 그라프트 공중합체의 경우 전분의 함량이 초기의 70% 정도로 감소하였음을 알 수 있었다. 공중합체 필름을 높은 상대습도하에서 보관한 결과 필름내 수분의 가소화작용에 의해 인장특성이 간소하였으며, 결정성 역시 점차 사라짐을 알 수 있었는데, 이는 필름내로 침투한 수분분자가 필름내부의 비정형부분을 팽윤시킨 다음 비교적 안정하지 못한 결정부분을 파괴시키기 때문이다. S-g-PMA 필름의 인장특성은 전분의 함량 뿐 만 아니라 전분의 조성비(아밀로스와 아밀로펙틴의 비)에 따라 달라짐을 보였는데, 고무상인 PMA의 함량 및 비교적 유연한 선형성의 아밀로스의 함량이 큰 공중합체필름의 경우 인장강도가 작고 파단신율이 큼을 알 수 있었다.

Keywords: