The charge accumulation characteristics of two types of PE/ionomer blends, PE/Surlyn 1652 blends and PE/Surlyn 1601 blends, have been investigated by measuring the spatial charge profiles. It was found that on dc stressing the heterocharges are accumulated in the LDPE while the homocharges are accumulated in the ionomers. After the voltage is turned off, however, a considerable amount of negative charge remains in the LDPE whereas almost no charges remain in the ionomers. In PE/ionomer blends the homocharges are accumulated during the application of dc stress. Upon removing the dc stress, most charges disappear in the case of PE/Surlyn 1652 blends while a considerable amount of charge migrates inside the specimen in the case of PE/Surlyn 1601 blends. The migration of charges into the bulk region might cause a decrease in TSC of PE/Surlyn 1601 blends at high fields. Besides, it was found trial the charge accumulation characteristics of PE/Surlyn 1601 blends was affected by the LDPE component whereas those of PE/Surlyn 1652 blends by the ionomer component.

두 종류의 PE/ionomer 블렌드, 즉 PE/Surlyn 1652 블렌드와 PE/Surlyn 1601 블렌드의 전하분포를 측정하여 두 블렌드에서의 전하축적특성에 대한 연구를 수행하였다. 전압이 가해지면 LDPE에서는 이종전하가 축적되는 반면 ionomer에서는 동종전하가 축적되며 전압이 제거되면 LDPE에는 상당량의 이종전하가 남는 반면 ionomer에는 극히 작은 양의 전하만이 남는다는 사실을 알았다. PE/ionomer 블렌드의 경우 전압을 가하면 두 블렌드에서 모두 동종전하의 주입이 일어나며, 전압을 제거하면 PE/Surlyn 1652 블렌드에서는 거의 모든 전하가 전극쪽으로 소멸되는데 비하여 PE/Surlyn 1601 블렌드에서는 상당량의 전하가 시료내로 이동하는 현상이 발견되었다. 전압 제거시 상당량의 전하가 시료내로 이동하는 현상이 PE/Surlyn 1601 블렌드의 TSC가 높은 전기장에서 감소하는 원인인 것으로 보인다. 이외에도 PE/Surlyn 1601 블렌드의 전하축적은 LDPE에 의하여 영향을 많이 받는 반면 PE/Surlyn 1652 블렌드는 ionomer에 의한 영향을 많이 받는 것으로 밝혀졌다.

Keywords: