Miscibility of a biodegradable polymer blend was reported in this work. Blends were prepared from vinylacetate(VA)-vinylpyrrolidone(VP) copolymers(PVAVP) and starch acetate (SA). The degree of acetylation and the intrinsic viscosity of starch acetate were observed to be 2.96 and 0.95, respectively. The intrinsic viscosities and g1ass transition temperatures(T_g) of the copolymers ranged 0.11-0.72 and 77.7-123.9℃, respectively, and decreased with increasing VA contents. PVAVP-Ⅱ/SA (20/80wt%) blend and PVAVP-Ⅳ/SA (30/70wt%) blend prepared by casting from chloroform solution showed two T_g's and the difference between the two T_g's of the blends was much lower than those of the two homopolymers. This result indicates that the blends with these compositions have partial miscibility. This fact was also supported by scanning electron micrographs.

초산비닐(VA)-비닐피로리돈(VP) 공중합체(PVAVP)와 아세틸화전분(SA)을 합성하고 이들의 블렌드의 상용성과 분해성을 조사하였다. 아세틸화전분의 아세틸화도 및 고유점도는 각각 2.96과 0.95로 측정되었고, 공중합체의 경우 고유점도는 0.11-0.72, 유리전이온도(T_g)는 77.7-123.9℃의 범위였으며 VA의 함량이 증가할수록 고유점도와 T_g가 감소하였다. 클로로포름용액으로 casting한 PVAVP-Ⅱ/SA (20/80wt%) 블렌드 및 PVAVP-Ⅳ/SA(30/70wt%) 블렌드는 두개의 T_g를 나타내었고 그 차이는 그 두가지 단독중합체의 T_g의 차이 보다 훨씬 작았다. 이 결과는 이 조성에서의 그 블렌드는 부분적인 상용성을 나타낸다는 것을 의미한다. 이 사실과 블렌드의 분해성이 전자현미경에 의해서 확인되었다.

Keywords: