Electrical conduction characteristics of low density polyethylene have been investigated using such contacts as silicone oil, semiconductive carbon black compound and sputtered Al. It was observed, as a result, the conduction characteristics change depending on the type of contacts. The major change was that the magnitudes of current densities, activation energies and effective charge mobilities were different depending on the type of contacts. It was also found that the conduction behavior of LDPE with the semiconductive contact is very similar to that with the sputtered Al contact. On the other hand, the silicone oil contact showed a low activation energy and a high effective charge mobility compared to those of sputtered Al contact. A more pronounced change due to the silicone-oil contact was a considerable suppression in s rate of change of current density at a certain voltage range. All observed changes due to the silicone-oil contacts were attributed to the interfacial polarization and subsequent charge sweeping effect enhanced by the accumulation of heterocharges.

폴리에틸렌과 전극사이의 접촉의 종류에 따른 폴리에틸렌의 전기전도 특성의 변화에 대하여 알아보았다. 본 연구에서 사용한 접촉은 실리콘유, 반도전성 카본블랙-고분자 복합체 및 sputter한 알루미늄 등이다. 실험결과 접촉의 종류에 따라 LDPE의 전류밀도, 활성화 에너지 및 유효전하이동도 등의 전도현상이 다르게 나타나는 것으로 밝혀졌다. 전력케이블의 내부반도전층 원료로 사용되고 있는 반도전 필름접촉의 전도특성이 sputter한 알루미늄 접촉의 전도특성과 매우 유사한 것으로 밝혀졌으나 실리콘유를 접촉으로 사용한 경우 상당히 다른 전도현상을 갖는다. 실리콘유를 접촉으로 사용한 경우 sputter한 경우에 비하여 활성화 에너지가 월등히 낮았으며 유효전하이동도는 약 2차수 이상 높은 값을 갖는다는 사실을 알았다. 실리콘유를 사용하였을 때 일어나는 현저한 변화는 일정한 전압구간에 걸쳐 전류밀도의 증가율이 감소하는 현상인데, 이 현상은 실리콘유를 접촉으로 사용했을 경우 이종전하의 축적으로 인한 계면분극 현상과 전하 sweeping 현상에 기인하는 것으로 생각된다.

Keywords: