  • Thermal, Mechanical and Rheological Properties of Ternary PC/ABS Blends
  • Lee IT, Kim BS, Park LS, Kwon YH, Chang JG
  • 3원 PC/ABS Blend의 열적, 기계적 성질 및 점도 거동
  • 이인태, 김병선, 박이순, 권영환, 장진규
Abstract
Ternary PC/ABS blends were prepared by direct melt blending of polycarbonate(PC). SAN and g-ABS copolymer of which the ABS resin is composed. As the content of PC was varied while maintaining SAN/g-ABS weight ratio of 85/15 (ABS-1) and 70/30 (ABS-2), the most distinguished improvement was observed in the notched Izod impact strength which was much higher than binary PC/ABS blend and even higher than pure PC polymer at optimum PC content of 60%. The effect of PC content and homogenous distribution of g-ABS by ternary PC/ABS blending on the other properties such as ultimate tensile strength, elongation and melt rheology are discussed case by case.

Polycarbonate(PC) 및 ABS 수지의 구성 성분인 SAN 및 g-ABS 공중합체를 용융 블렌딩하여, 3원 고분자 합금 형태의 PC/ABS 블렌드를 제조하고 열적, 기계적 및 점도 성질을 조사하였다. SAN/g-ABS의 조성비를 85/15 및 70/30의 일정 비율로 유지하면서 PC의 함량을 변화시켰을 때, 가장 뛰어난 성질은 충격강도의 증가로서 PC가 60%인 경우는 2원 PC/ABS 합금보다는 물론 순수한 PC보다 높은 충격강도를 나타내었다. 이외에도 PC함량의 변화 및 3원 합금법에 따른 g-ABS의 균일한 분포가 인장 강도, 연신율 및 점도 거동에 미치는 영향을 고찰하였다.

References
  • 1. Paul DR, Newman SPolymer Blends, Academic Press, Inc., New York (1978)
  •  
  • 2. Manson JA, Sperling LHPolymer Blends and Composites, Plenum, New York (1976)
  •  
  • 3. Grabowski TSU.S. Patent, 3,130,177 (1964)
  •  
  • 4. Bucknall CBToughened Plastics, Applied Science Publishers, London (1977)
  •  
  • 5. Angola JC, Fujika Y, Sakai T, Inoue T, J. Polym. Sci. B: Polym. Phys., 26, 807 (1988)
  •  
  • 6. Suarez H, Barlow JW, Paul DR, J. Appl. Polym. Sci., 29, 3253 (1984)
  •  
  • 7. Kurauchi T, Ohta T, J. Mater. Sci., 19, 1699 (1984)
  •  
  • 8. Deanin RD, Chu CW, J. Elast. Plast., 18, 42 (1986)
  •  
  • 9. Kim WN, burns CM, Polym. Eng. Sci., 28, 1115 (1988)
  •  
  • 10. Kim WN, Burns CM, J. Appl. Polym. Sci., 34, 945 (1987)
  •  
  • 11. Sawyer LC, Grubb DTPolymer Microscopy, Chapman and Hall, New York (1987)
  •  
  • 12. Stefan D, Williams HL, J. Appl. Polym. Sci., 18, 145 (1974)
  •  
  • 13. Han CDRheology in Polymer Processing, Academic Press, Inc., New York (1976)
  •  
  • 14. Weber G, Schoeps J, Angew. Makromol. Chem., 136, 45 (1985)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1991; 15(2): 141-146

    Published online Apr 25, 1991