  • Studies on the Designed Latex and Emulsion Polymerization 2. Inverse Emulsion Polymerization of Acrylamide Comonomers
  • Park LS, Lee YH, Back TM, Hwang JJ
  • Designed Latex 및 유화중합에 관한 연구 2. 아크릴아미드 공단량체들의 역유화 중합반응
  • 박이순, 이용훈, 백태무, 황정재
Abstract
Water-soluble copolymer, poly(acrylamide-co-sodium acrylate) , was synthesized by the inverse emulsion polymerization method. It was found that incorporation of high HLB (hydrophilic-lyophilic balance) coemulsifier in addition to the water-in-oil type main emulsifier increased the rate of polymerization significantly. Some type of phase transfer catalyst also increased the polymer conversion significantly. The emulsifier mixture system with bulky Iyophilic group resulted in good latex stability possibly due to formation of a steric barrier which prevented the particles from agglomerating.

아크릴아미드와 아크릴산 나트륨 단량체의 몰비를 70 : 30으로 하여 poly(acryamide-co-sodium acrylate) 중합체를 역유화 중합법(inverse emulson polymerization)으로 중합할 때 혼합유화제계가 중합반응 및 생성된 라텍스의 안정성에 미치는 영향을 조사하였다. 실험의 결과 water-in-oil형 주유화제 (main emulsifier)를 단독으로 사용하는 경우보다 친수성-친유성 비(HLB) 값이 높은 조유화제 (coemulsifier)들을 첨가할 때 중합 전환율이 향상됨을 알았다. 또 몇 종류의 상 전이 촉매들도 중합 전환율을 현저히 향상 시킴을 보았다. 혼합 유화제계를 쓴 경우 생성된 라텍스의 안정성은 주유화제 및 조유화제들의 친유성기들의 입체적 부피 (bulkiness)가 큰 경우 안정성이 증가였으며 이러한 영향은 주유화제에 의한 안정화가 조유화제에 의한 것보다 더 크게 나타났다.

References
  • 1. Thomas WMEncyclo. of Polym. Sci. & Eng., New York, Vol. 1, page 162-211 (1985)
  •  
  • 2. Volk H, Friedlich RE, Davidson RLHandbook of Water Soluble Gums and Resins, John Wiley & Sons, New York, p. 298-311 (1978)
  •  
  • 3. Kulicke WM, Klein J, Angew. Makromol. Chem., 69, 169 (1978)
  •  
  • 4. Pellon JJ, Savoy PEU.S. Patent, 4,242,247 (1980)
  •  
  • 5. Vanderhoff JW, Adv. Chem. Ser., 34, 32 (1962)
  •  
  • 6. Vanderhoff JW, Wiley RMU.S. Patent, 3,284,393 (1966)
  •  
  • 7. Glukhikk C, J. Polym. Sci. A: Polym. Chem., 25, 1127 (1987)
  •  
  • 8. Anderson DR, Frisque AJU.S. Patent, 3,826,771 (1974)
  •  
  • 9. Candau F, Macromolecules, 19, 1895 (1986)
  •  
  • 10. Graillat C, J. Polym. Sci. A: Polym. Chem., 24, 427 (1986)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1990; 14(6): 583-589

    Published online Dec 25, 1990