The miscibility of poly (butylene terephthalate) with polyurethane-PBT multiblock copolymers (BC''s) of various PBT block contents was studied. The blends of PBT with BC''s Containing 50, 75, or 90wt% PBT block had a good miscibility showing a sing1e g1ass transition temperature, whereas the blends with the BC''s containing 10 or 25wt% PBT block had a partial miscibility showing two glass transition temperatures correponding to component polymers. This difference in miscibility due to the different content of PBT block in BC was also observed by scanning electron microscopy. The melting point depression of PBT in blends was increased with increasing the PBT block in BC, and the crystallization rate of PBT in blends was greatly retarded by the added BC.

Poly(butylene terephthalate) (PBT)와 polyurethane-PBT multiblock 공중합체 (BC)의 상용성을 BC중 각 블록의 함량을 변화시키면서 조사하였다. BC중 PBT블록의 함량이 50, 75, 90wt% 경우 두 고분자는 한개의 유리전이온도 (T_g)를 갖는 좋은 상용성을 가졌으며, PBT 블록의 함량이 10, 25wt%인 경우는 두 구성 고분자의 Tg가 이동된 위치에서 각각 독립적으로 나타나는 부분적 상용성을 자졌다. 이러한 상용성의 변화는 주사전자 현미경으로 관찰한 morphology 에서도 확인할 수 있었다. 블렌드물에서 PBT의 녹는점은 BC중 PBT블록의 함량이 증가할수록 크게 감소하는 경향을 보았으여, PBT의 결정화속도는 가해진 BC에 의해 크게 지연되었다.