The artificial skin for wound covering materials was prepared from gelatin, poly-(vinyl alcohol) and poly(2-hydroxyethyl methacrylate). Their mechanical properties under dry and wet state, water content, permeability of water vapor and rate of in vitro degradation by protease Ⅳ were evaluated. This artificial skin was covered on the full- thickness skin wound on the back of rats and their effect of wound healing was investigated by histological evaluation as a function of time. All the properties of artificial skin was found to be enough for the desired properties of an ideal artificial skin. The result of animal test showed that the formation of scar on the surface was markedly minimized. Also the neoepidermal tissue was regenerated between the artificial skin and the wound surface after 10 days of grafting operation.

Gelatin, poly(vinyl alcohol)과 poly(2-hydroxyethyl methacrylate)로 부터 화상치료용 인공피부를 제조하였다. 제조된 인공피부의 건조시 및 습윤시의 기계적 성질, 함수율, 수분투과도와 protease Ⅳ에 의한 생분해속도를 측정하였다. 이 인공피부를 쥐의 등부위의 피부전층 상처에 대해 피복하고 시간에 따른 상처 치유효과를 조직학적 평가에 의해 검토하였다. 인공피부의 모든 성질은 이상적인 인공피부의 성질과 유사하였다. 동물실험 결과, 상처 표면의 흉터 형성을 상당히 감소시키는 것을 보여 주었다. 또한 피복수술 10일 후의 조직사진으로부터 인공피부와 상처표면 사이에 새로운 표피조직이 형성된 것을 알 수 있었다.