Thermal behavior of incompatible PS/HDPE blonds is characterized by DSC thermogram. Crystallinity and heat of fusion of the blend are increased with the HDPE content. Overlapping of peaks by PS glass transition and HDPE melting prevents from using the onset point as characteristic temperature. Instead, the deflection point (temperture where the second derivative of energy flow against temperature becomes zero ) after the onset and the peak temperture are used to examine the thermal behavior of PS/HDPE blends. The deflection temperature is linearly increased with the HDPE content, However, the peak temperature shown a mild maximum at PS/HDPE=30/70, which may be attributable to the phase morphology of the blend. That is, at a given heating rate of l0℃/min, particle size and spacing of the dispersed phase (PS), and the low heat capacity of HDPE medium could be balanced to yield a maximum at PS/ HDPE=30/70. When one neglects the variation of peak temperature for the high HDPE content (70% or more), these HDPE-rich blends may have a constant peak temperature while the deflection point is varied linearly with PS content.

비상용성 PS/HDPE 블렌드와 열적성질을 DSC로 측정하였다. 블렌드의 결정화도와 융해열은 HDPE의 함량이 증가함에 따라 증가한다. PS의 유리전이온도와 HDPE의 녹는 온도가 서로 가깝게 중첩되어 onsets 온도를 특성온도로 사용할 수 없다. 대신 onset 온도후 변곡점(열의 흐름이 온도에 대한 제2차 미분이 영이 되는 온도)과 최저온도를 PS/HDPE 블렌드의 열적거동을 조사하는데 사용하였다. 변곡점은 HDPE 함량의 증가에 따라 거의 직선적으로 증가한다. 그러나 최저온도는 PS/HOPE=30/70에서 완만한 최고값을 주고 있는데, 블렌드의 형태학과 연관성이 있다고 사료된다. 즉 주어진 10℃/min의 가열속도에서 분산상인 PS의 입사크기와 입자간의 간격, 그리고 연속상인 HDPE의 낮은 비열 등의 균형으로 PS/HDPE=30/70에서 최대가 나타난다고 판단된다. 70%이상의 HDPE를 포함한 블렌드의 최저온도에 대한 변화를 무시할 때, 이들 블렌드는 일정한 최저은도를 갖지만 변곡점은 PS함량과 직선적인 관계에 있다고도 할 수 있다.