The miscibility behaviors of poly(methyl methacrylate) (PMMA) and polystyrene (PS) with polyarylate(PAR)were studied by observing the change of glass transition temperature(T_g) in the blends. PMMA/PAR and PS/PAR blends had both a partial miscibility showing two separate T_g''s slightly migrated toward each other. The PMMA contents in PAR-rich phase changed about 10wt.% with the molecular weight of PMMA (M_w of PMMA:50,000-150,000). but the PS contents in PAR-rich phase did not changed so much with the molecular weight of PS(M_w of PS:30,000-300,000). When the composition of PAR in blends was in the range of 70-8Owt.%, the dispersed particles of PMMA-rich and Ps-rich phase had the diameter of about 1μ.

Poly(methyl methacrylate) (PMMA)와 polystyrene(PS)의 polyarylate(PAR)와의 상용성을 구성 고분자의 분자량과 조성을 변화시키면서 유리전이온도(T_g)의 변화로부터 관찰하였다. PMMA/PAR, PS/PAR계 모두 부분적 상용성을 보였으며 PAR-rich상 중에 PMMA가 녹아 들어가는 정도는 PMMA의 분자량이 50,000-150,000 범위에서 약 10wt.% 정도의 큰 변화를 보이는데 반해 PAR-rich 상중에 PS가 녹아 들어가는 정도는 PS 분자량이 30,000-300,000의 범위에서 변화하여도 큰 변화를 보이지 않았다. 또 PAR의 조성이 많은 경우(70-80wt.%)PMMA-rich 상과 PS-rich상은 1μ크기 정도의 입자로 PAR-rich상 중에 분산하고 있음을 주사전자현미경에서 관찰할 수 있었다.