Polyurethane(PU)-poly(butylene terephthalate) (PBT) multiblock copolymers (BC''S) were synthesized from PBT oligoester,1,4-butandiol, and methylene-bis- (4-phenylisocyanate). The change of thermal properties due to the change of the content or the molecular weight of PBT block in BC was studied. BC''s, quenched after melting, have a single glass transition temperature(T_g), which shows that the length of the blocks in BC is not long enough to occur sufficient phase separation. Melting temperature(T_m) and crystallization temperature (T_mc ) were increased with the content of the PU block in BC. From the thermal properties, such as T_g or T_m. better separation of phase was observed in the BC synthesized from PBT oligoester of larger molcular weight.

Poly(butylene terephthalate)(PBT) oligoester, 1,4-butanediol, 그리고 methylenebis- (4-phenylisocyanate)를 반응시켜 Polyurethane (PU)-PBT multiblock 공중합체 (BC)를 합성하고, BC중 PBT block의 함량과 분자량의 변화에 따른 열적 성질의 변화를 관찰하였다. 용융 후 급냉시킨 BC에서 한개의 유리전이온도 (T_g)를 관찰할 수 있었으며. 이는 각 block의 길이가 짧아 충분한 상분리가 일어나지 못함을 보여준다. 녹는점 (T_m)과 결정화 온도(T_mc)는 PU domain의 함량이 증가함에 따라 증가하는 경향을 보였다. 한편 PBT block의 함량이 일정한 경우, PBT block의 분자량이 클수록 PBT domain과 PU domain의 상분리가 큼을 T_g, T_m 으로 부터 관찰할 수 있었다.