Viscoelastic properties of SAN-based composites. i.e., SAN/PPTA, SAN/KF and SAN/CF have been determined from a Rheovibron and RDS Rheometer as well. Reinforcing effects of PPTA and KF were much greater compared to those of CF, and this was interpreted in terms of strong interaction between SAN and PPTA, and SAN and KF. Strong interaction via hydrogen bonding was also confirmed from FTIR measurements. A significant difference was also true between SAN/PPTA, a molecular composite prepared from solution blending, and SAN/KF, a fiber reinforced composite, with much greater effect for the former at low filler concentration. This is presumably due to the microfibril formation of PPTA in SAN matrix leading to a fine dispersion with more hydrogen bonding chance, attested from FTIR measurement.

SAN을 기초로한 복합재료인 SAN/PPTA, SAN/KF 및 SAN/탄소섬유 복합재료를 제조, 이들의 점탄성적 성질을 Rheovibron 및 RDS Rheometer로부터 측정하였다. PPTA 및 KF는 SAN과 수소결합을 통한 계면인력의 증대로 탄소섬유에 비하여 보강효과가 현저하였으며, 이들의 수소결합 형성을 FTIR로 확인하였다. 또한 용액 블렌드로 제조한 분자복합재료인 SAN/PPTA는 섬유강화 복합재료인 SAN/KF에 비하여 같은 농도에서 보다 우수한 보강효과를 나타내었다. 이는 PPTA가 SAN 연속상내에서 마이크로 피브릴을 형성, 보다 미세하게 분산되므로 수소결합의 가능성이 보다 큰 데 기인하는 것으로 믿어지며, FTIR측정은 이를 뒷받침 해주었다.