  • Copolyester Studies V. Crystallization Behaviours of Poly(ethylene terephthalate) Modified by Poly(ethylene glycol) Unit
  • Ahn TO, Kim OY, Jeong HM
  • Poly(ethylene glycol) Unit로 개질된 Poly(ethylene terephthalate)의 결정화 거동
  • 안태완, 김오영, 정한모
Abstract
The crystallization behaviours of poly(ethylene terephthalate) modified by poly(ethylene glycol) of molecular weight 300(PHG-300) were studied by isothermal and nonisothermal crystallization. When crystallized nonisothermally, the cold crystallization and the melt crystallization temperature were much decreased with the content of PEG-300. In isothermal crystallization, the crystallization rate at a definite temperature was much decreased with the content of PEG-300, but at the same supercooling the rate was increased by the added PEG-300 at the content less than 10mol% and decreased again at the content more than 10mol%. The Avrami indices at the same supercooling were almost the same and independent of the contents Of PEG-300. Which shows the crystallization mechanism of copolyesters is almost the same.

PEG-300을 제3의 단량체로 PET를 개질한 copolyester를 비등온 결정화 시킨 경우 PEG-300 의 함량이 증가함에 따나 Tcc, Tmc가 크게 감소하였으며, 일정온도에서 등온결정화 시킨 경우 PEG-300의 함량이 증가함에 따라 결정화 속도는 크게 지연되었으나, 동일과냉각 상태에서의 결정화속도는 PEG-300의 함량에 따라 증가하였다 감소하는 경향을 보였다. 이러한 변화는 PEG-300이 쇄의 유연성을 증가시켜 copolyester의 결정화속도를 증가시키는 효과와 결정할 수 없는 타성분으로 작용하여 copolyester의 결정화 속도를 지연시키는 효과가 함께 나타남에 기인하는 것으로 생각된다. 또 동일한 과냉각 상태에서 Avrami index는 PEG-300치 함량에 따자 거의 변화하지 않았는데 이는 copolyester의 결정화기구가 PEG-300의 함량에 무관하게 거의 동일함을 보여준다.

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1987; 11(6): 540-546

    Published online Dec 25, 1987