  • Study on the Thermal Treatment of a Wholly Aromatic Polyester
  • Lee SH, Park HJ
  • 전 방향족 폴리에스테르의 열처리에 관한 연구
  • 이석현, 박호진
Abstract
A fully aromatic polyester based on chlorohydroquinone and terephthalic acid modified with 4,4''-biphenol and isophthalic acid was prepared by polycondensation reaction. These polymers showed thermotropic liquid crystal behavior, which was evidenced by DSC and X -ray diffraction experiments. Thermal treatment of these polymers was performed under various atomospheres as a function of annealing time and the time -temperature relationship of heat treatment process was examined. The experimental results examined by DSC showed that the peak temperatures are shifted progressively to higher temperature and the peak areas are increased by extending the annealing time. As a result of solid -state polymerization, the melting behavior of heat treated specimens depended significantly on the environmental conditions X-ray results revealed that a heat treated specimen has an orthorhombic unit cell (a ; 6.4 A, b : A, c ; 23.1 A)and further experiments should be under-taken to confirm and refine the tentatively proposed cell parameters.

클로로 히드로 퀴곤 및 테레프탈산을 주로 하고 4,4 -비페놀과 이소프탈산을 소량 첨가시켜 축합 중합에 의하여 전 방향족 폴리에스테르를 합성하였다. DSC 및 X-건 회절 실험으로부터 이들 고분자가 열방성 액정임을 확인하였다. 다양한 분위기에서 열처리 시간을 변화시켜 열처리하였으며 열처리 공정의 시간-온도 관계를 검토하였다. 상기 시편을 DSC로 조사한 결과에 따르면 결정의 용점이나 피크면적은 점진적으로 열처리 시간이 길어짐에 따라 증가하였으며, 열처리 과정에서 일어나는 고상 중합 때문에 용응거동이 열처리 분위기의 영향을 많이 받았다. 한편, X-선 실험결과에 의하면 상기 열처리 된 고분자는 Orthorhombic unit cell (a ; 6.4 A, b ,4.6 A, c ; 23.1 A)을 가지며 이르 격자 상수를 확인하고 보다 더 정교하기 위해서는 더 많은 실험이 진행되어야 할 것으로 생각된다.

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1987; 11(5): 411-416

    Published online Oct 25, 1987